Magnetic tape, magnetic tape cartridge, and magnetic tape device

ABSTRACT

A magnetic tape in which a tape thickness of the magnetic tape is 5.2 μm or less, and in an environment with a temperature of 32° C. and a relative humidity of 80%, a frictional force F 45°  on the surface of the magnetic layer with respect to an LTO8 head measured at a head tilt angle of 45° is 4 gf to 15 gf, and a standard deviation of a frictional force F on the surface of the magnetic layer with respect to the LTO8 head measured at each of head tilt angles of 0°, 15°, 30°, and 45° is 10 gf or less.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority under 35 U.S.C. 119 to Japanese Patent Application No. 2021-158783 filed on Sep. 29, 2021 and Japanese Patent Application No. 20022-135815 filed on Aug. 29, 2022. Each of the above applications is hereby expressly incorporated by reference, in its entirety, into the present application.

BACKGROUND OF THE INVENTION 1. Field of the Invention

The present invention relates to a magnetic tape, a magnetic tape cartridge, and a magnetic tape device.

2. Description of the Related Art

Magnetic recording media are divided into tape-shaped magnetic recording media and disk-shaped magnetic recording media, and tape-shaped magnetic recording media, that is, magnetic tapes are mainly used for data storage such as data back-up or archives (for example, see JP2016-524774A and US2019/0164573A1).

SUMMARY OF THE INVENTION

The recording of data on a magnetic tape is normally performed by causing the magnetic tape to run in a magnetic tape device and causing a magnetic head to follow a data band of the magnetic tape to record data on the data band. Accordingly, a data track is formed on the data band. In addition, in a case of reproducing the recorded data, the magnetic tape is caused to run in the magnetic tape device and the magnetic head is caused to follow the data band of the magnetic tape, thereby reading data recorded on the data band.

In order to increase an accuracy with which the magnetic head follows the data band of the magnetic tape in the recording and/or the reproducing, a system that performs head tracking using a servo signal (hereinafter, referred to as a “servo system”) is practiced.

In addition, it is proposed that dimensional information of a magnetic tape during running in a width direction (contraction, expansion, or the like) is obtained using the servo signal and an angle for tilting an axial direction of a module of a magnetic head with respect to the width direction of the magnetic tape (hereinafter, also referred to as a “head tilt angle”) is changed according to the obtained dimensional information (see JP6590102B and US2019/0164573A1, for example, paragraphs 0059 to 0067 and paragraph 0084 of JP6590102B). During the recording or the reproducing, in a case where the magnetic head for recording or reproducing data records or reproduces data while being deviated from a target track position due to width deformation of the magnetic tape, phenomenons such as overwriting on recorded data, reproducing failure, and the like may occur. The present inventors consider that changing the head tilt angle as described above is one of a unit for suppressing the occurrence of such a phenomenon.

For example, assuming that the head tilt angle is changed as described above, it is desirable that running stability of the magnetic tape is high, in a case of recording and/or reproducing data at different head tilt angles. It is considered that the high running stability of the magnetic tape can lead to, for example, the further suppressing of the occurrence of the phenomenon described above.

Meanwhile, in recent years, magnetic tapes may be used in temperature and humidity managed data centers.

Meanwhile, in the data center, power saving is necessary for reducing the cost. For realizing the power saving, it is desired that the management conditions of an use environment of the magnetic tape in the data center can be relaxed compared to the current state, or the managing may not be necessary.

However, it is also assumed that, in a case where the management conditions of the use environment are relaxed or not managed, the magnetic tape is used, for example, in a high temperature and high humidity environment. Accordingly, a magnetic tape having excellent running stability in a case of recording and/or reproducing data at different head tilt angles in a high temperature and high humidity environment is desirable.

One aspect of the present invention is to provide a magnetic tape having excellent running stability in a case of recording and/or reproducing data at different head tilt angles in a high temperature and high humidity environment.

An aspect of the invention is as follows.

-   (1) A magnetic tape comprising:

a non-magnetic support; and

a magnetic layer containing a ferromagnetic powder,

wherein a tape thickness of the magnetic tape is 5.2 μm or less,

in an environment with a temperature of 32° C. and a relative humidity of 80%,

a frictional force F_(45°) on a surface of the magnetic layer with respect to a Linear Tape-Open (LTO) 8 head measured at a head tilt angle of 45° is 4 gf to 15 gf, and

a standard deviation of a frictional force F on the surface of the magnetic layer with respect to the LTO8 head measured at each of head tilt angles of 0°, 15°, 30°, and 45° (hereinafter, also simply referred to as a “standard deviation of a frictional force F” or a “standard deviation of F”) is 10 gf or less.

-   (2) The magnetic tape according to (1),

wherein the standard deviation of F is 2 gf to 10 gf.

-   (3) The magnetic tape according to (1) or (2),

wherein the tape thickness is 4.0 μm to 5.2 μm.

-   (4) The magnetic tape according to any one of (1) to (3),

wherein the tape thickness is 4.0 μm to 5.0 μm.

-   (5) The magnetic tape according to any one of (1) to (4),

wherein a standard deviation of curvature of the magnetic tape in a longitudinal direction (hereinafter, also simply referred to as a “standard deviation of curvature”) is 5 mm/m or less.

-   (6) The magnetic tape according to any one of (1) to (5),

wherein the magnetic layer contains inorganic oxide-based particles.

-   (7) The magnetic tape according to (6),

wherein the inorganic oxide-based particles are composite particles of an inorganic oxide and a polymer.

-   (8) The magnetic tape according to any one of (1) to (5),

wherein the magnetic layer contains carbon black.

-   (9) The magnetic tape according to any one of (1) to (8), further     comprising:

a non-magnetic layer containing a non-magnetic powder between the non-magnetic support and the magnetic layer.

-   (10) The magnetic tape according to (9),

wherein a thickness of the non-magnetic layer is 0.1 μm to 0.7 μm.

-   (11) The magnetic tape according to any one of (1) to (10), further     comprising:

a back coating layer containing a non-magnetic powder on a surface side of the non-magnetic support opposite to a surface side provided with the magnetic layer.

-   (12) The magnetic tape according to any one of (1) to (11),

wherein a vertical squareness ratio of the magnetic tape is 0.60 or more.

-   (13) The magnetic tape according to any one of (1) to (12),

wherein a vertical squareness ratio of the magnetic tape is 0.60 or more.

-   (14) A magnetic tape cartridge comprising:

the magnetic tape according to any one of (1) to (13),

-   (15) A magnetic tape device comprising:

the magnetic tape according to any one of (1) to (13).

-   (16) The magnetic tape device according to (15), further comprising:

a magnetic head,

wherein the magnetic head includes a module having an element array including a plurality of magnetic head elements between a pair of servo signal reading elements, and

the magnetic tape device changes an angle θ formed by an axis of the element, array with respect to a width direction of the magnetic tape during running of the magnetic tape in the magnetic tape device.

According to one aspect of the present invention, it is possible to provide a magnetic tape having excellent running stability in a case of recording and/or reproducing data at different head tilt angles in a high temperature and high humidity environment. In addition, according to one aspect of the invention, it is possible to provide a magnetic tape cartridge and a magnetic tape device including the magnetic tape.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic view showing an example of a module of a magnetic head.

FIG. 2 is an explanatory diagram of a relative positional relationship between a module and a magnetic tape during running of the magnetic tape in a magnetic tape device.

FIG. 3 is an explanatory diagram of a change in angle θ during the running of the magnetic tape.

FIG. 4 is an explanatory diagram of a curvature of a magnetic tape in a longitudinal direction.

FIG. 5 shows an example of disposition of data bands and servo bands.

FIG. 6 shows a servo pattern disposition example of a linear tape-open (LTO) Ultrium format tape.

FIG. 7 is an explanatory diagram of a method for measuring the angle θ during the running of the magnetic tape.

FIG. 8 is a schematic view showing an example of the magnetic tape device.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Magnetic Tape

An aspect of the invention relates to a magnetic tape including a non-magnetic support, and a magnetic layer containing a ferromagnetic powder. A tape thickness of the magnetic tape is 5.2 μm or less. In addition, in an environment with a temperature of 32° C. and a relative humidity of 80%, regarding a frictional force on a surface of the magnetic layer with respect to an LTO8 head of the magnetic tape, a frictional force F_(45°) on the surface of the magnetic layer with respect to the LTO8 head measured at a head tilt angle of 45° is 4 gf to 15 gf, and a standard deviation of a frictional force F on the surface of the magnetic layer with respect to the LTO8 head measured at each of head tilt angles of 0°, 15°, 30°, and 45° is 10 gf or less. In the invention and the specification, the “surface of the magnetic layer” is identical to a surface of the magnetic tape on the magnetic layer side. In addition, in terms of unit, “gf” represents grain weight and 1 N (Newton) is approximately 102 gf.

Head Tilt Angle

For describing the head tilt angle, first, the LTO8 head will be described hereinafter. In addition, a reason why it is considered that the phenomenon occurring during the recording or during the reproducing described above can be suppressed by tilting an axial direction of the module of the magnetic head with respect to the width direction of the magnetic tape while the magnetic tape is running will also be described later.

In the invention and the specification, the “LTO8 head” is a magnetic head according to the LTO8 standard. For the measurement of the frictional force, a magnetic head mounted on an LTO8 drive may be extracted and used, or a commercially available magnetic head may he used as the magnetic head for the LTO drive. Here, the LTO8 drive is a drive (magnetic tape device) according to the LTO8 standard. The LTO9 drive is a drive according to the LTO9 standard, and the same applies to drives of other generations. In addition, in a case of measuring a frictional force F on the surface of the magnetic layer with respect to the LTO8 head at each of head tilt angles of 0°, 15°, 30°, and 45°, in the measurement at each head tilt angle, new (that is, unused) LTO8 head is used for each measurement. In addition, the LTO8 is used as a head for measuring the frictional force considering that the LTO8 standard is the standard that can cope with high-density recording in recent years, and the magnetic tape is not limited to a magnetic tape used in the LTO8 drive. The magnetic tape may perform the recording and/or reproducing of data in the LTO8 drive, may perform the recording and/or reproducing of data in the LTO9 drive or a next-generation drive, or may perform the recording and/or reproducing of data in a drive in earlier generations of the LTO8 such as LTO7.

The LTO8 head includes three modules each having an element array including a plurality of magnetic head elements between a pair of servo signal reading elements. The three modules are arranged in the LTO8 head in arrangement of “recording module-reproducing module-recording module” (total number of modules: 3).

Each module includes an element array including 32 magnetic head elements in total between a pair of servo signal reading elements, that is, arrangement of elements. The module including a recording element as the magnetic head element is a recording module for recording data on the magnetic tape. The module including a reproducing element as the magnetic head element is a reproducing module for reproducing data recorded on the magnetic tape. In the LTO8 head, the three modules are arranged so that an axis of the element array of each module is oriented in parallel. The “parallel” does not mean only parallel in the strict sense, but also includes a range of errors normally allowed in the technical field of the invention. For example, the range of errors means a range of less than ±10° from an exact parallel direction.

The head tilt angle in the frictional force measurement is a head tilt angle of the LTO8 head in the reproducing module.

In each element array, the pair of servo signal reading elements and the plurality of magnetic head elements (that is, recording elements or reproducing elements) are arranged to be in a straight line spaced apart from each other. Here, the expression that “arranged in a straight line” means that each magnetic head element is arranged on a straight line connecting a central portion of one servo signal reading element and a central portion of the other servo signal reading element. The “axis of the element array” in the present invention and the present specification means the straight line connecting the central portion of one servo signal reading element and the central portion of the other servo signal reading element.

Next, the configuration of the module and the like will be further described with reference to the drawings. However, the aspect shown in the drawings is an example and the invention is not limited thereto.

FIG. 1 is a schematic view showing an example of a module of a magnetic head. The module shown in FIG. 1 includes a plurality of magnetic head elements between a pair of servo signal reading elements (servo signal reading elements 1 and 2). The magnetic head element is also referred to as a “channel”. “Ch” in the drawing is an abbreviation for a channel. The module shown in FIG. 1 includes a total of 32 magnetic head elements of Ch0 to Ch31. The reproducing module of the LTO8 head includes a total of 32 reproducing elements of Ch0 to Ch31.

In FIG. 1 , “L” is a distance between the pair of servo signal reading elements, that is, a distance between one servo signal reading element and the other servo signal reading element. In the module shown in FIG. 1 , the “L” is a (distance between the servo signal reading element 1 and the servo signal reading element 2. Specifically, the “L” is a distance between a central portion of the servo signal reading element 1 and a central portion of the servo signal reading element 2. Such a distance can be measured by, for example, an optical microscope or the like.

FIG. 2 is an explanatory diagram of a relative positional relationship between the module and the magnetic tape during running of the magnetic tape in the magnetic tape device. In FIG. 2 , a dotted line A indicates a width direction of the magnetic tape. A dotted line B indicates an axis of the element array. An angle θ can be the head tilt angle during the running of the magnetic tape, and is an angle formed by the dotted line A and the dotted line B. During the running of the magnetic tape, in a case where the angle θ is 0°, a distance in a width direction of the magnetic tape between one servo signal reading element and the other servo signal reading element of the element array (hereinafter, also referred to as an “effective distance between servo signal reading elements”) is “L”. On the other hand, in a case where the angle θ exceeds 0°, the effective distance between the servo signal reading elements is “Lcosθ” and the Lcosθ is smaller than the L. That is, “Lcosθ<L”.

As described above, during the recording or the reproducing, in a case where the magnetic head for recording or reproducing data records or reproduces data while being deviated from a target track position due to width deformation of the magnetic tape, phenomenons such as overwriting on recorded data, reproducing failure, and the like may occur. For example, in a case where a width of the magnetic tape contracts or extends, a phenomenon may occur in which the magnetic head element that should record or reproduce at a target track position records or reproduces at a different track position. In addition, in a case where the width of the magnetic tape extends, the effective distance between the servo signal reading elements may be shortened than a spacing of two adjacent servo bands with a data band interposed therebetween (also referred to as a “servo band spacing” or “spacing of servo bands”, specifically, a distance between the two servo bands in the width direction of the magnetic tape), and a phenomenon in that the data is not recorded or reproduced at a part close to an edge of the magnetic tape can occur.

With respect to this, in a case where the element array is tilted at the angle θ exceeding 0°, the effective distance between the servo signal reading elements becomes “Lcos θ” as described above. The larger the value of θ, the smaller the value of Lcos θ, and the smaller the value of θ, the larger the value of Lcos θ. Accordingly, in a case where the value of θ is changed according to a degree of dimension change (that is, contraction or expansion) in the width direction of the magnetic tape, the effective distance between the servo signal reading elements can be brought closer to or matched with the spacing of the servo bands. Therefore, during the recording or the reproducing, it is possible to prevent the occurrence of phenomenons such as overwriting on recorded data, reproducing failure, and the like caused in a case where the magnetic head for recording or reproducing data records or reproduces data while being deviated from a target track position due to width deformation of the magnetic tape, or it is possible to reduce a frequency of occurrence thereof.

FIG. 3 is an explanatory diagram of a change in angle θ dining the running of the magnetic tape.

The angle θ at the start of running, θ_(initial), can be set to, for example, 0° or more or more than 0°.

In FIG. 3 , a central diagram shows a state of the module at the start of running.

In FIG. 3 , a right diagram shows a state of the module in a case where the angle θ is set to an angle θ_(c) which is a larger angle than the θ_(initial). The effective distance between the servo signal reading elements Lcosθ_(c) is a value smaller than Lcosθ_(initial) at the start of running of the magnetic tape. In a case where the width of the magnetic tape is contracted during the running of the magnetic tape, it is preferable to perform such angle adjustment.

On the other hand, in FIG. 3 , a left diagram shows a state of the module in a case where the angle θ is set to an angle θ_(c) which is a smaller angle than the θ_(initial). The effective distance between the servo signal reading elements Lcosθ_(c) is a value larger than Lcosθ_(initial) at the start of running of the magnetic tape. In a case where the width of the magnetic tape is expanded during the running of the magnetic tape, it is preferable to perform such angle adjustment.

As described above, the change of the head tilt angle during the running of the magnetic tape can contribute to prevention of the occurrence of phenomenons such as overwriting on recorded data, reproducing failure, and the like caused in a case where the magnetic head for recording or reproducing data records or reproduces data while being deviated from a target track position due to width deformation of the magnetic tape, or to reduction of a frequency of occurrence thereof.

Meanwhile, the recording of data on the magnetic tape and the reproducing of the recorded data are performed by bringing the surface of the magnetic layer of the magnetic tape into contact with the magnetic head and sliding. The inventors considered that, during such sliding, in a case where the head tilt angle changes, a contact state between the magnetic head and the surface of the magnetic layer can change and this can be a reason of a decrease in running stability. Specifically, the inventors surmised that, in a case where the contact state between the surface of the magnetic layer of the magnetic tape and the magnetic head (for example, a contact state between a portion near an edge of the module of the magnetic head and the surface of the magnetic layer) changes greatly depending on the difference in the head tilt angle, the running stability decreases and such decrease in running stability can become more remarkable in a high temperature and high humidity environment.

Based on the surmise described above, the present inventors conducted intensive studies. As a result, it is newly found that, regarding the friction property of the magnetic tape, in the environment with the temperature of 32° C. and the relative humidity of 80%, by setting the frictional force F_(45°) on the surface of the magnetic layer with respect to the LTO8 head measured at the head tilt angle 45°, and the standard deviation of the frictional force F on the surface of the magnetic layer with respect to the LTO8 head measured at each of the head tilt angles of 0°, 15°, 30°, and 45° to be in the ranges described above, respectively, it is possible to improve running stability in a case of performing the recording and/or reproducing of data at different head tilt angles in the high temperature and high humidity environment. The temperature and humidity of the measurement environment are used as exemplary values of the temperature and humidity of the high temperature and high humidity environment. Accordingly, the environment in which the data is recorded on the magnetic tape and the recorded data is reproduced is not limited to the environment with the temperature and the humidity described above. The head tilt angle in a case of measuring the frictional force is also used as an exemplary value of the angle that can be used in a case of performing the recording and/or reproducing of data by changing the head tilt angle during the running of the magnetic tape. Accordingly, the head tilt angle in a case where the data is recorded on the magnetic tape and the recorded data is reproduced is not limited to the angle described above. In addition, the present invention is not limited to the inference of the inventors described in the present specification.

In the following, the running stability in a case of performing the recording and/or reproducing of data by changing the head tilt angle during the running of the magnetic tape in the high temperature and high humidity environment is also simply referred to as “running stability”. In addition, the high temperature and high humidity environment can be, for example, an environment having a temperature of approximately 30° C. to 50° C. A humidity of the environment can be, for example, approximately 70% to 100% as a relative humidity. The temperatures and the humidity described for the environment in the invention and the specification are an atmosphere temperature and a relative humidity of such an environment.

In the invention and the specification, the measurement of the frictional force at each of the head tilt angles of 0°, 15°, 30°, and 45° is performed by the following method in the environment with the temperature of 32° C. and the relative humidity of 80%.

In addition, the head tilt angle for the frictional force measurement is an angle formed by an axis of the element array of the reproducing module of the LTO8 head with respect to a direction orthogonal to a sliding direction in a first outward path of the following 100 reciprocating slides. Such an angle is read as a direction orthogonal to the sliding direction in FIG. 2 , and is an angle θ formed by A and B. The head tilt angle is fixed during the 100 reciprocating slides.

The magnetic tape to be measured is placed on two cylindrical guide rolls having a diameter of 1 inch (1 inch=2.54 cm) spaced from each other and arranged in parallel with each other so that the surface of the magnetic layer comes into contact therewith. In a randomly extracted portion of the magnetic tape to be measured, the surface of the magnetic layer of the magnetic tape is caused to slide on the LTO8 head with the head tilt angle of 0°, 15°, 30°, or 45°, and a resistance force generated during the sliding is detected by a strain gauge. The reciprocating sliding is performed 100 times. For the measurement conditions, a lap angle θ is set to 6° and a sliding speed is set to 30 mm/sec. A tension applied in the longitudinal direction of the magnetic tape during the sliding is 0.55 N. Each sliding distance of the outward path and a return path is set to 5 cm. A dynamic frictional force in the 100th outward path is set to the frictional force at each head tilt angle. During the measurement, one end of both ends of the magnetic tape to be measured in the longitudinal direction is connected to the strain gauge, and a tension of 0.20 N is applied to the other end thereof. The frictional force F value is calculated by the following equation, where the tension applied here is defined as T₀ (unit: N) and the resistance force detected by the strain gauge is defined as T (unit: N). That is, here, the frictional force F is calculated as T₀=0.20. The measurement of the frictional forces F at the four head tilt angles is performed at different parts of the magnetic tape to be measured in a random order. In addition, before each measurement, in order to be familiar with the measurement environment, the magnetic tape to be measured is left on the guide roll as described above for 24 hours or longer. The standard deviation (that is, a positive square root of the variance) is calculated from the values of the frictional forces F at the four head tilt angles.

F=T−T ₀

Frictional Force F_(45°) and Standard Deviation of Frictional Force F

Regarding the friction property of the magnetic tape, the frictional force F_(45°) is 4 gf to 15 gf, from a viewpoint of improving running stability in a case of the recording and/or reproducing of data at different head tilt angles in the high temperature and high humidity environment. From a viewpoint of further improving the running stability, the frictional force F_(45°) is preferably 14 gf or less, more preferably 13 gf, even more preferably 12 gf or less, and still preferably 11 gf or less. The frictional force F_(45°) is 4 gf or more, and is preferably 5 gf or more, from a viewpoint of further improving the running stability.

The standard deviation of the frictional force F on the magnetic layer surface with respect to the LTO8 head measured at each of head tilt angles 0°, 15°, 30°, and 45° is 10 gf or less, preferably 9 gf or less, more preferably 8 gf or less, even more preferably 7 gf or less, still preferably 6 gf or less, still more preferably 5 gf or less, and still even more preferably 4 gf or less, from a viewpoint of improving the running stability in a case of performing the recording and/or reproducing at different head tilt angles in the high temperature and high humidity environment. The standard deviation can be, for example, 0 gf or greater, greater than 0 gf, 1 gf or greater, or 2 gf or greater. It is preferable that the value of the standard deviation is small, from a viewpoint of further improving the running stability.

The friction property of the magnetic tape can be adjusted, for example, according to a kind of component used for manufacturing the magnetic layer. The details of this point will be described later.

Tape Thickness

Regarding a tape thickness (total thickness) of the magnetic tape, it has been required to increase recording capacity, that is, increase in capacity of the magnetic tape along with the enormous increase in amount of information in recent years. From a viewpoint of achieving high capacity, the tape thickness of the magnetic tape is 5.2 μm or less. By reducing the tape thickness of the magnetic tape, for example, a length of the magnetic tape accommodated in one reel of the magnetic tape cartridge can be increased, and accordingly, the high capacity can be achieved. From a viewpoint of further increasing high capacity, the tape thickness of the magnetic tape is preferably 5.0 μm or less and more preferably 4.8 μm or less. In addition, from a viewpoint of ease of handling, the tape thickness of the magnetic tape is preferably 3.0 μm or more, more preferably 3.5 μm or more, and even more preferably 4.0 μm or more.

In the present invention and the present specification, the tape thickness of e magnet tape is measured by the following method.

Ten tape samples (for example, length of 5 to 10 cm) are cut out from a random portion of the magnetic tape, these tape samples are overlapped, and the thickness is measured. A value which is one tenth of the measured thickness (thickness per one tape sample) is set as the tape thickness. The thickness measurement can be performed using a well-known measurement device capable of performing the thickness measurement at 0.1 μm order.

Standard Deviation of Curvature

Next, a standard deviation of a curvature will be described.

The curvature of the magnetic tape in the longitudinal direction of the present invention and the present specification is a value obtained by the following method in an environment of an atmosphere temperature of 23° C. and a relative humidity of 50%. The magnetic tape is normally accommodated and circulated in a magnetic tape cartridge. As the magnetic tape to be measured, a magnetic tape taken out from an unused magnetic tape cartridge that is not attached to the magnetic tape device is used.

FIG. 4 is an explanatory diagram of the curvature of the magnetic tape in the longitudinal direction.

A tape sample having a length of 100 m in the longitudinal direction is cut out from a randomly selected portion of the magnetic tape to be measured. One end of this tape sample is defined as a position of 0 m, and a position spaced apart from this one end toward the other end by D m (D meters) in the longitudinal direction is defined as a position of D m. Accordingly, a position spaced apart by 10 m in the longitudinal direction is defined as a position of 10 m, a position spaced apart by 20 m is defined as a position of 20 m, and in this manner, a position of 30 m, a position of 40 m, a position of 50 m, a position of 60 m, a position of 70 m, a position of 80 m, a position of 90 m, and a position of 100 m are defined at intervals of 10 m sequentially.

A tape sample having a length of 1 m from the 0 m position to the position of 1 m is cut out. This tape sample is used as a tape sample for measuring the curvature at the position of 0 m.

A tape sample having a length of 1 m from the 10 m position to the position of 11 m is cut out. This tape sample is used as a tape sample for measuring the curvature at the position of 10 m.

A tape sample having a length of 1 m from the 20 m position to the position of 21 m is cut out. This tape sample is used as a tape sample for measuring the curvature at the position of 20 m.

A tape sample having a length of 1 m from the 30 m position to the position of 31 m is cut out. This tape sample is used as a tape sample for measuring the curvature at the position of 30 m.

A tape sample having a length of 1 m from the 40 m position to the position of 41 m is cut out. This tape sample is used as a tape sample for measuring the curvature at the position of 40 m.

A tape sample having a length of 1 m from the 50 m position to the position of 51 m is cut out. This tape sample is used as a tape sample for measuring the curvature at the position of 50 m.

A tape sample having a length of 1 m from the 60 m position to the position of 61 m is cut out. This tape sample is used as a tape sample for measuring the curvature at the position of 60 m.

A tape sample having a length of 1 m from the 70 m position to the position of 71 m is cut out. This tape sample is used as a tape sample for measuring the curvature at the position of 70 m.

A tape sample having a length of 1 m from the 80 m position to the position of 81 m is cut out. This tape sample is used as a tape sample for measuring the curvature at the position of 80 m.

A tape sample having a length of 1 m from the 90 m position to the position of 91 m is cut out. This tape sample is used as a tape sample for measuring the curvature at the position of 90 m.

A tape sample having a length of 1 m from the 99 m position to the position of 100 m is cut out. This tape sample is used as a tape sample for measuring the curvature at the position of 100 m.

The tape sample of each position is hung for 24 hours±4 hours in a tension-free state by gripping an upper end portion with a gripping member (clip or the like) by setting the longitudinal direction as the vertical direction. Then, within 1 hour, the following measurement is performed.

As shown in FIG. 4 , the tape piece is placed on a flat surface in a tension-free state. The tape piece may be placed on a flat surface with the surface on the magnetic layer side facing upward, or may be placed on a flat surface with the other surface facing upward. In FIG. 4 , S indicates a tape sample and W indicates the width direction of the tape sample. Using an optical microscope, a distance L1 (unit: mm) that is a shortest distance between a virtual line 54 connecting both terminal portions 52 and 53 of the tape sample S and a maximum curved portion 55 in the longitudinal direction of the tape sample S is measured. FIG. 4 shows an example in which the tape sample is curved upward on a paper surface. Even in a case where the tape sample is curved downward, the distance L1 (mm) is measured in the same manner. The distance L1 is displayed as a positive value regardless of which side is curved. In a case where no curve in the longitudinal direction is confirmed, the L1 is set to 0 (zero) mm.

By doing so, a standard deviation of the curvature L1 measured for a total of 11 positions from the position of 0 m to the position of 100 m (that is, a positive square root of the dispersion) is the standard deviation of the curvature of the magnetic tape to be measured in the longitudinal direction (unit: mm/m).

In the magnetic tape, the standard deviation of the curvature obtained by the method described above can be, for example, 7 mm/m or less and 6 mm/m or less, and from a viewpoint of further improving the running stability, it is preferably 5 mm/m or less, more preferably 4 mm/m or less, and even more preferably 3 mm/m or less. The standard deviation of the curvature of the magnetic tape can be, for example, 0 mm/m or more, more than 0 mm/m, 1 mm/m or more, or 2 mm/m or more. It is preferable that the value of the standard deviation of the curvature is small, from a viewpoint of further improving the running stability.

The standard deviation of the curvature can be controlled by adjusting the manufacturing conditions of the manufacturing step of the magnetic tape. This point will be described later in detail.

Hereinafter, the magnetic tape will be described more specifically.

Magnetic Layer

Ferromagnetic Powder

As the ferromagnetic powder contained in the magnetic layer, a well-known ferromagnetic powder can be used as one kind or in combination of two or more kinds as the ferromagnetic powder used in the magnetic layer of various magnetic recording media. It is preferable to use a ferromagnetic powder having an average particle size as the ferromagnetic powder, from a viewpoint of improvement of a recording density. From this viewpoint, an average particle size of the ferromagnetic powder is preferably equal to or smaller than 50 nm, more preferably equal to or smaller than 45 nm, even more preferably equal to or smaller than 40 nm, further preferably equal to or smaller than 35 nm, further more preferably equal to or smaller than 30 nm, further even more preferably equal to or smaller than 25 nm, and still preferably equal to or smaller than 20 nm. Meanwhile, from a viewpoint of stability of magnetization, the average particle size of the ferromagnetic powder is preferably equal to or greater than 5 nm, more preferably equal to or greater than 8 nm, even more preferably equal to or greater than 10 nm, still preferably equal to or greater than 15 nm, and still more preferably equal to or greater than 20 nm.

Hexagonal Ferrite Powder

As a preferred specific example of the ferromagnetic powder, a hexagonal ferrite powder can be used. For details of the hexagonal ferrite powder, descriptions disclosed in paragraphs 0012 to 0030 of JP2011-225417A, paragraphs 0134 to 0136 of JP2011-216149A, paragraphs 0013 to 0030 of JP2012-204726A, and paragraphs 0029 to 0084 of JP2015-127985A can be referred to, for example.

In the invention and the specification, the “hexagonal ferrite powder” is a ferromagnetic powder in which a hexagonal ferrite type crystal structure is detected as a main phase by X-ray diffraction analysis. The main phase is a structure to which a diffraction peak at the highest intensity in an X-ray diffraction spectrum obtained by the X-ray diffraction analysis belongs. For example, in a case where the diffraction peak at the highest intensity in the X-ray diffraction spectrum obtained by the X-ray diffraction analysis belongs to a hexagonal ferrite type crystal structure, it is determined that the hexagonal ferrite type crystal structure is detected as a main phase. In a case where only a single structure is detected by the X-ray diffraction analysis, this detected structure is set as a main phase. The hexagonal ferrite type crystal structure includes at least an iron atom, a divalent metal atom, and an oxygen atom as constituting atoms. A divalent metal atom is a metal atom which can be divalent cations as ions, and examples thereof include an alkali earth metal atom such as a strontium atom, a barium atom, or a calcium atom, and a lead atom. In the invention and the specification, the hexagonal strontium ferrite powder is powder in which a main divalent metal atom included in this powder is a strontium atom, and the hexagonal barium ferrite powder is a powder in which a main divalent metal atom included in this powder is a barium atom. The main divalent metal atom is a divalent metal atom occupying the greatest content in the divalent metal atom included in the powder based on atom %. However, the divalent metal atom described above does not include rare earth atom. The “rare earth atom” of the invention and the specification is selected front the group consisting of a scandium atom (Sc), an yttrium atom (Y), and a lanthanoid atom. The lanthanoid atom is selected from the group consisting of a lanthanum atom (La), a cerium atom (Ce), a praseodymium atom (Pr), a neodymium atom (Nd), a promethium atom (Pm), a samarium atom (Sin), an europium atom (Eu), a gadolinium atom (Gd), a terbium atom (Tb), a dysprosium atom (Dy), a holmium atom (Ho), an erbium atom (Er), a thulium atom (Tm), an ytterbium atom (Yb), and a lutetium atom (Lu).

Hereinafter, the hexagonal strontium ferrite powder which is one aspect of the hexagonal ferrite powder will be described more specifically.

An activation volume of the hexagonal strontium ferrite powder is preferably in a range of 800 to 1,600 nm³. The atomized hexagonal strontium ferrite powder showing the activation volume in the range described above is suitable for manufacturing a magnetic tape exhibiting excellent electromagnetic conversion characteristics. The activation volume of the hexagonal strontium ferrite powder is preferably equal to or greater than 800 nm³, and can also be, for example, equal to or greater than 850 nm³. In addition, from a viewpoint of further improving the electromagnetic conversion characteristics, the activation volume of the hexagonal strontium ferrite powder is more preferably equal to or smaller than 1,500 nm³, even more preferably equal to or smaller than 1,400 nm³, still preferably equal to or smaller than 1,300 nm³, still more preferably equal to or smaller than 1,200 nm³, and still even more preferably equal to or smaller than 1,100 nm³. The same applies to the activation volume of the hexagonal barium ferrite powder.

The “activation volume” is a unit of magnetization reversal and an index showing a magnetic magnitude of the particles. Regarding the activation volume and an anisotropy constant Ku which will be described later disclosed in the invention and the specification, magnetic field sweep rates of a coercivity Hc measurement part at time points of 3 minutes and 30 minutes are measured by using an oscillation sample type magnetic-flux meter (measurement temperature: 23° C.±1° C.), and the activation volume and the anisotropy constant Ku are values acquired from the following relational expression of Hc and an activation volume V. A unit of the anisotropy constant Ku is 1 erg/cc=1.0×10⁻¹ J/m³.

Hc=2 Ku/Ms {1-[(kT/KuV)In(At/0.693)]^(1/2)}

[In the expression, Ku: anisotropy constant (unit: J/m³), Ms: saturation magnetization (unit: kA/m), k: Boltzmann's constant, T: absolute temperature (unit: K), V: activation volume (unit: cm³), A: spin precession frequency (unit: s⁻¹), and t: magnetic field reversal time (unit: s)]

The anisotropy constant Ku can be used as an index of reduction of thermal fluctuation, that is, improvement of thermal stability. The hexagonal strontium ferrite powder can preferably have Ku equal to or greater than 1.8×10⁵ J/m³, and more preferably have Ku equal to or greater than 2.0×10⁵ J/m³. In addition, Ku of the hexagonal strontium ferrite powder can be, for example, equal to or smaller than 2.5×10⁵ J/m³. However, the high Ku is preferable, because it means high thermal stability, and thus, Ku is not limited to the exemplified value.

The hexagonal strontium ferrite powder may or may not include the rare earth atom. In a case where the hexagonal strontium ferrite powder includes the rare earth atom, a content (bulk content) of the rare earth atom is preferably 0.5 to 5.0 atom % with respect to 100 atom % of the iron atom. In one embodiment, the hexagonal strontium ferrite powder including the rare earth atom can have a rare earth atom surface layer portion uneven distribution. The “rare earth atom surface layer portion uneven distribution” of the invention and the specification means that a content of rare earth atom with respect to 100 atom % of iron atom in a solution obtained by partially dissolving the hexagonal strontium ferrite powder with acid (hereinafter, referred to as a “rare earth atom surface layer portion content” or simply a “surface layer portion content” regarding the rare earth atom) and a content of rare earth atom with respect to 100 atom % of iron atom in a solution obtained by totally dissolving the hexagonal strontium ferrite powder with acid (hereinafter, referred to as a “rare earth atom bulk content” or simply a “bulk content” regarding the rare earth atom) satisfy a ratio of rare earth atom surface layer portion content/rare earth atom bulk content >1.0.

The content of rare earth atom of the hexagonal strontium ferrite powder which will be described later is identical to the rare earth atom bulk content. With respect to this, the partial dissolving using acid is to dissolve the surface layer portion of particles configuring the hexagonal strontium ferrite powder, and accordingly, the content of rare earth atom in the solution obtained by the partial dissolving is the content of rare earth atom in the surface layer portion of the particles configuring the hexagonal strontium ferrite powder. The rare earth atom surface layer portion content satisfying a ratio of “rare earth atom surface layer portion content/rare earth atom bulk content >1.0” means that the rare earth atoms are unevenly distributed in the surface layer portion (that is, a larger amount of the rare earth atoms is present, compared to that inside), among the particles configuring the hexagonal strontium ferrite powder. The surface layer portion of the invention and the specification means a part of the region of the particles configuring the hexagonal strontium ferrite powder towards the inside from the surface.

In a case where the hexagonal strontium ferrite powder includes the rare earth atom, a content (bulk content) of the rare earth atom is preferably in a range of 0.5 to 5.0 atom % with respect to 100 atom % of the iron atom. It is thought that the rare earth atom having the bulk content in the range described above and uneven distribution of the rare earth atom in the surface layer portion of the particles configuring the hexagonal strontium ferrite powder contribute to the prevention of a decrease in reproducing output during the repeated reproducing. It is surmised that this is because the rare earth atom having the hulk content in the range described above included in the hexagonal strontium ferrite powder and the uneven distribution of the rare earth atom in the surface layer portion of the particles configuring the hexagonal strontium ferrite powder can increase the anisotropy constant Ku. As the value of the anisotropy constant Ku is high, occurrence of a phenomenon called thermal fluctuation (that is, improvement of thermal stability) can be prevented. By preventing the occurrence of the thermal fluctuation, a decrease in reproducing output during the repeated reproducing can he prevented. It is surmised that the uneven distribution of the rare earth atom in the surface layer portion of the particles of the hexagonal strontium ferrite powder contributes to stabilization of a spin at an iron (Fe) site in a crystal lattice of the surface layer portion, thereby increasing the anisotropy constant Ku.

In addition, it is surmised that the use of the hexagonal strontium ferrite powder having the rare earth atom surface layer portion uneven distribution as the ferromagnetic powder of the magnetic layer also contributes to the prevention of chipping of the surface of the magnetic layer due to the sliding with the magnetic head. That is, it is surmised that, the hexagonal strontium ferrite powder having the rare earth atom surface layer portion uneven distribution can also contribute to the improvement of running durability of the magnetic tape. It is surmised that this is because the uneven distribution of the rare earth atom on the surface of the particles configuring the hexagonal strontium ferrite powder contributes to improvement of an interaction between the surface of the particles and an organic substance (for example, binding agent and/or additive) included in the magnetic layer, thereby improving hardness of the magnetic layer.

From a viewpoint of preventing reduction of the reproduction output in the repeated reproduction and/or a viewpoint of further improving running durability, the content of rare earth atom (bulk content) is more preferably in a range of 0.5 to 4.5 atom %, even more preferably in a range of 1.0 to 4.5 atom % and still preferably in a range of 1.5 to 4.5 atom %.

The bulk content is a content obtained by totally dissolving the hexagonal strontium ferrite powder. In the invention and the specification, the content of the atom is a bulk content obtained by totally dissolving the hexagonal strontium ferrite powder, unless otherwise noted. The hexagonal strontium ferrite powder including the rare earth atom may include only one kind of rare earth atom or may include two or more kinds of rare earth atom, as the rare earth atom. In a case where two or more kinds of rare earth atoms are included, the bulk content is obtained from the total of the two or more kinds of rare earth atoms. The same also applies to the other components of the invention and the specification. That is, for a given component, only one kind may be used or two or more kinds may be used, unless otherwise noted. In a case where two or more kinds are used, the content is a content of the total of the two or more kinds.

In a case where the hexagonal strontium ferrite powder includes the rare earth atom, the rare earth atom included therein may be any one or more kinds of the rare earth atom. Examples of the rare earth atom preferable from a viewpoint of preventing reduction of the reproduction output during the repeated reproduction include a neodymium atom, a samarium atom, an yttrium atom, and a dysprosium atom, a neodymium atom, a samarium atom, an yttrium atom are more preferable, and a neodymium atom is even more preferable.

In the hexagonal strontium ferrite powder having the rare earth atom surface layer portion uneven distribution, a degree of uneven distribution of the rare earth atom is not limited, as long as the rare earth atom is unevenly distributed in the surface layer portion of the particles configuring the hexagonal strontium ferrite powder. For example, regarding the hexagonal strontium ferrite powder having the rare earth atom surface layer portion uneven distribution, a ratio of the surface layer portion content of the rare earth atom obtained by partial dissolving performed under the dissolving conditions which will be described later and the bulk content of the rare earth atom obtained by total dissolving performed under the dissolving conditions which will be described later, “surface layer portion content/bulk content” is greater than 1.0 and can be equal to or greater than 1.5. The “surface layer portion content/bulk content” greater than 1.0 means that the rare earth atoms are unevenly distributed in the surface layer portion (that is, a larger amount of the rare earth atoms is present, compared to that inside), in the particles configuring the hexagonal strontium ferrite powder. A ratio of the surface layer portion content of the rare earth atom obtained by partial dissolving performed under the dissolving conditions which will be described later and the bulk content of the rare earth atom obtained by total dissolving performed under the dissolving conditions which will be described later, “surface layer portion content/bulk content” can be, for example, equal to or smaller than 10.0, equal to or smaller than 9.0, equal to or smaller than 8.0, equal to or smaller than 7.0, equal to or smaller than 6.0, equal to or smaller than 5.0, or equal to or smaller than 4.0. However, in the hexagonal strontium ferrite powder having the rare earth atom surface layer portion uneven distribution, the “surface layer portion content/bulk content” is not limited to the exemplified upper limit or the lower limit, as long as the rare earth atom is unevenly distributed in the surface layer portion of the particles configuring the hexagonal strontium ferrite powder.

The partial dissolving and the total dissolving of the hexagonal strontium ferrite powder will be described below. Regarding the hexagonal strontium ferrite powder present as the powder, sample powder for the partial dissolving and the total dissolving are collected from powder of the same batch. Meanwhile, regarding the hexagonal strontium ferrite powder included in a magnetic layer of a magnetic tape, a part of the hexagonal strontium ferrite powder extracted from the magnetic layer is subjected to the partial dissolving and the other part is subjected to the total dissolving. The extraction of the hexagonal strontium ferrite powder from the magnetic layer can be performed by, for example, a method disclosed in a paragraph 0032 of JP2015-91747A.

The partial dissolving means dissolving performed so that the hexagonal strontium ferrite powder remaining in the solution can be visually confirmed in a case of the completion of the dissolving. For example, by performing the partial dissolving, a region of the particles configuring the hexagonal strontium ferrite powder which is 10% to 20% by mass with respect to 100% by mass of a total of the particles can be dissolved. On the other hand, the total dissolving means dissolving performed until the hexagonal strontium ferrite powder remaining in the solution is not visually confirmed in a case of the completion of the dissolving.

The partial dissolving and the measurement of the surface layer portion content are, for example, performed by the following method. However, dissolving conditions such as the amount of sample powder and the like described below are merely examples, and dissolving conditions capable of performing the partial dissolving and the total dissolving can be randomly used.

A vessel (for example, beaker) containing 12 mg of sample powder and 10 mL of hydrochloric acid having a concentration of 1 mol/L is held on a hot plate at a set temperature of 70° C. for 1 hour. The obtained solution is filtered with a membrane filter having a hole diameter of 0.1 μm. The element analysis of the filtrate obtained as described above is performed by an inductively coupled plasma (ICP) analysis device. By doing so, the surface layer portion content of the rare earth atom with respect to 100 atom % of the iron atom can be obtained. In a case where a plurality of kinds of rare earth atoms are detected from the element, analysis, a total content of the entirety of the rare earth atoms is the surface layer portion content. The same applies to the measurement of the bulk content.

Meanwhile, the total dissolving and the measurement of the bulk content are, for example, performed by the following method.

A vessel (for example, beaker) containing 12 mg of sample powder and 10 mL of hydrochloric acid having a concentration of 4 mol/L is held on a hot plate at a set temperature of 80° C. for 3 hours. After that, the process is performed in the same manner as in the partial dissolving and the measurement of the surface layer portion content, and the bulk content with respect to 100 atom % of the iron atom can be obtained.

From a viewpoint of increasing reproducing output in a case of reproducing data recorded on a magnetic tape, it is desirable that the mass magnetization σs of ferromagnetic powder included in the magnetic tape is high. In regards to this point, in hexagonal strontium ferrite powder which includes the rare earth atom but does not have the rare earth atom surface layer portion uneven distribution, σs tends to significantly decrease, compared to that in hexagonal strontium ferrite powder not including the rare earth atom. With respect to this, it is thought that, hexagonal strontium ferrite powder having the rare earth atom surface layer portion uneven distribution is also preferable for preventing such a significant decrease in σs. In one aspect, σs of the hexagonal strontium ferrite powder can be equal to or greater than 45 A×m²/kg and can also be equal to or greater than 47 A×m²/kg. On the other hand, from a viewpoint of noise reduction, σs is preferably equal to or smaller than 80 A×m²/kg and more preferably equal to or smaller than 60 A×m²/kg. σs can be measured by using a well-known measurement device capable of measuring magnetic properties such as an oscillation sample type magnetic-flux meter. In the invention and the specification, the mass magnetization σs is a value measured at a magnetic field strength of 15 kOe, unless otherwise noted. 1 [kOe]=(10⁶/4λ) [A/m]

Regarding the content (bulk content) of the constituting atom in the hexagonal strontium ferrite powder, a content of the strontium atom can be, for example, in a range of 2.0 to 15.0 atom % with respect to 100 atom % of the iron atom. In one aspect, in the hexagonal strontium ferrite powder, the divalent metal atom included in this powder can be only a strontium atom. In another aspect, the hexagonal strontium ferrite powder can also include one or more kinds of other divalent metal atoms, in addition to the strontium atom. For example, the hexagonal strontium ferrite powder can include a barium atom and/or a calcium atom. In a case where the other divalent metal atom other than the strontium atom is included, a content of a barium atom and a content of a calcium atom in the hexagonal strontium ferrite powder respectively can be, for example, in a range of 0.05 to 5.0 atom % with respect to 100 atom % of the iron atom.

As the crystal structure of the hexagonal ferrite, a magnetoplumbite type (also referred to as an “M type”), a W type, a Y type, and a Z type are known. The hexagonal strontium ferrite powder may have any crystal structure. The crystal structure can be confirmed by X-ray diffraction analysis. In the hexagonal strontium ferrite powder, a single crystal structure or two or more kinds of crystal structure can be detected by the X-ray diffraction analysis. For example, in one aspect, in the hexagonal strontium ferrite powder, only the M type crystal structure can be detected by the X-ray diffraction analysis. For example, the M type hexagonal ferrite is represented by a compositional formula of AFe₁₂O₁₉. Here, A represents a divalent metal atom, in a case where the hexagonal strontium ferrite powder has the M type, A is only a strontium atom (Sr), or in a case where a plurality of divalent metal atoms are included as A, the strontium atom (Sr) occupies the hexagonal strontium ferrite powder with the greatest content based on atom % as described above. A content of the divalent metal atom in the hexagonal strontium ferrite powder is generally determined according to the type of the crystal structure of the hexagonal ferrite and is not particularly limited. The same applies to a content of an iron atom and a content of an oxygen atom. The hexagonal strontium ferrite powder at least includes an iron atom, a strontium atom, and an oxygen atom, and can also include a rare earth atom. In addition, the hexagonal strontium ferrite powder may or may not include atoms other than these atoms. As an example, the hexagonal strontium ferrite powder may include an aluminum atom (Al). A content of the aluminum atom can be, for example, 0.5 to 10.0 atom % with respect to 100 atom % of the iron atom. From a viewpoint of preventing the reduction of the reproduction output during the repeated reproduction, the hexagonal strontium ferrite powder includes the iron atom, the strontium atom, the oxygen atom, and the rare earth atom, and a content of the atoms other than these atoms is preferably equal to or smaller than 10.0 atom %, more preferably in a range of 0 to 5.0 atom %, and may be 0 atom % with respect to 100 atom % of the iron atom. That is, in one aspect, the hexagonal strontium ferrite powder may not include atoms other than the iron atom, the strontium atom, the oxygen atom, and the rare earth atom. The content shown with atom % described above is obtained by converting a value of the content (unit: % by mass) of each atom obtained by totally dissolving the hexagonal strontium ferrite powder into a value shown as atom % by using the atomic weight of each atom. In addition, in the invention and the specification, a given atom which is “not included” means that the content thereof obtained by performing total dissolving and measurement by using an ICP analysis device is 0% by mass. A detection limit of the ICP analysis device is generally equal to or smaller than 0.01 ppm (parts per million) based on mass. The expression “not included” is used as a meaning including that a given atom is included with the amount smaller than the detection limit of the ICP analysis device. In one aspect, the hexagonal strontium ferrite powder does not include a bismuth atom (Bi).

Metal Powder

As a preferred specific example of the ferromagnetic powder, a ferromagnetic metal powder can also be used. For details of the ferromagnetic metal powder, descriptions disclosed in paragraphs 0137 to 0141 of JP2011-216149A and paragraphs 0009 to 0023 of JP2005-25151A can be referred to, for example.

ε-Iron Oxide Powder

As a preferred specific example of the ferromagnetic powder, an ε-iron oxide powder can also be used. In the invention and the specification, the “ε-iron oxide powder” is a ferromagnetic powder in which an ε-iron oxide type crystal structure is detected as a main phase by X-ray diffraction analysis. For example, in a case where the diffraction peak at the highest intensity in the X-ray diffraction spectrum obtained by the X-ray diffraction analysis belongs to an ε-iron oxide type crystal structure, it is determined that the ε-iron oxide type crystal structure is detected as a main phase. As a manufacturing method of the ε-iron oxide powder, a manufacturing method from a goethite, a reverse micelle method, and the like are known. All of the manufacturing methods are well known. For the method of manufacturing the ε-iron oxide powder in which a part of Fe is substituted with substitutional atoms such as Ga, Co, Ti, Al, or Rh, a description disclosed in J. Jpn. Soc. Powder Metallurgy Vol. 61 Supplement, No. S1, pp. S280-S284, J. Mater. Chem. C, 2013, 1, pp.5200-5206 can be referred, for example. However, the manufacturing method of the ε-iron oxide powder capable of being used as the ferromagnetic powder in the magnetic layer of the magnetic tape is not limited to the method described here.

An activation volume of the ε-iron oxide powder is preferably in a range of 300 to 1,500 nm³. The atomized ε-iron oxide powder showing the activation volume in the range described above is suitable for manufacturing a magnetic tape exhibiting excellent electromagnetic conversion characteristics. The activation volume of the ε-iron oxide powder is preferably equal to or greater than 300 nm³, and can also be, for example, equal to or greater than 500 nm³. In addition, from a viewpoint of further improving the electromagnetic conversion characteristics, the activation volume of the ε-iron oxide powder is more preferably equal to or smaller than 1,400 nm³, even more preferably equal to or smaller than 1,300 nm³, still preferably equal to or smaller than 1,200 nm³, and still more preferably equal to or smaller than 1,100 nm³.

The anisotropy constant Ku can be used as an index of reduction of thermal fluctuation, that is, improvement of thermal stability. The ε-iron oxide powder can preferably have Ku equal to or greater than 3.0×10⁴ J/m³, and more preferably have Ku equal to or greater than 8.0×10⁴ J/m³. In addition, Ku of the ε-iron oxide powder can be, for example, equal to or smaller than 3.0×10⁵ J/m³. However, the high Ku is preferable, because it means high thermal stability, and thus, Ku is not limited to the exemplified value.

From a viewpoint of increasing reproducing output in a case of reproducing data recorded on a magnetic tape, it is desirable that the mass magnetization σs of ferromagnetic powder included in the magnetic tape is high. In regard to this point, in one aspect, σs of the ε-iron oxide powder can be equal to or greater than 8 A×m²/kg and can also be equal to or greater than 12 A×m²/kg. On the other hand, from a viewpoint of noise reduction, σs of the ε-iron oxide powder is preferably equal to or smaller than 40 A×m²/kg and more preferably equal to or smaller than 35 A×m²/kg.

In the invention and the specification, average particle sizes of various powder such as the ferromagnetic powder and the like are values measured by the following method with a transmission electron microscope, unless otherwise noted.

The powder is imaged at an imaging magnification ratio of 100,000 with a transmission electron microscope, the image is printed on photographic printing paper or displayed on a display so that the total magnification ratio of 500,000 to obtain an image of particles configuring the powder. A target particle is selected from the obtained image of particles, an outline of the particle is traced with a digitizer, and a size of the particle (primary particle) is measured. The primary particle is an independent particle which is not aggregated.

The measurement described above is performed regarding 500 particles arbitrarily extracted. An arithmetic mean of the particle size of 500 particles obtained as described above is the average particle size of the powder. As the transmission electron microscope, a transmission electron microscope H-9000 manufactured by Hitachi, Ltd. can be used, for example. In addition, the measurement of the particle size can be performed by a well-known image analysis software, for example, image analysis software KS-400 manufactured by Carl Zeiss. The average particle size shown in examples which will be described later is a value measured by using transmission electron microscope H-9000 manufactured by Hitachi, Ltd. as the transmission electron microscope, and image analysis software KS-400 manufactured by Carl Zeiss as the image analysis software, unless otherwise noted. In the invention and the specification, the powder means an aggregate of a plurality of particles. For example, the ferromagnetic powder means an aggregate of a plurality of ferromagnetic particles. The aggregate of the plurality of particles not only includes an aspect in which particles configuring the aggregate are directly in contact with each other, but also includes an aspect in which a binding agent or an additive which will be described later is interposed between the particles. A term, particles may be used for representing the powder.

As a method for collecting a sample powder from the magnetic tape in order to measure the particle size, a method disclosed in a paragraph of 0015 of JP2011-048878A can be used, for example.

In the invention and the specification, unless otherwise noted,

(1) in a case where the shape of the particle observed in the particle image described above is a needle shape, a fusiform shape, or a columnar shape (here, a height is greater than a maximum long diameter of a bottom surface), the size (particle size) of the particles configuring the powder is shown as a length of a major axis configuring the particle, that is, a major axis length,

(2) in a case where the shape of the particle is a planar shape or a columnar shape (here, a thickness or a height is smaller than a maximum long diameter of a plate surface or a bottom surface), the particle size is shown as a maximum long diameter of the plate surface or the bottom surface, and

(3) in a case where the shape of the particle is a sphere shape, a polyhedron shape, or an unspecified shape, and the major axis configuring the particles cannot be specified front the shape, the particle size is shown as an equivalent circle diameter. The equivalent circle diameter is a value obtained by a circle projection method.

In addition, regarding an average acicular ratio of the powder, a length of a minor axis, that is, a minor axis length of the particles is measured in the measurement described above, a value of (major axis length/minor axis length) of each particle is obtained, and an arithmetic mean of the values obtained regarding 500 particles is calculated. Here, unless otherwise noted, in a case of (1), the minor axis length as the definition of the particle size is a length of a minor axis configuring the particle, in a case of (2), the minor axis length is a thickness or a height, and in a case of (3), the major axis and the minor axis are not distinguished, thus, the value of (major axis length/minor axis length) is assumed as 1, for convenience.

In addition, unless otherwise noted, in a case where the shape of the particle is specified, for example, in a case of definition of the particle size (1), the average particle size is an average major axis length, and in a case of the definition (2), the average particle size is an average plate diameter. In a case of the definition (3), the average particle size is an average diameter (also referred to as an average particle diameter).

The content (filling percentage) of the ferromagnetic powder of the magnetic layer is preferably in a range of 50% to 90% by mass and more preferably in a range of 60% to 90% by mass with respect to a total mass of the magnetic layer. A high filling percentage of the ferromagnetic powder in the magnetic layer is preferable from a viewpoint of improvement of recording density.

Binding Agent

The magnetic tape may be a coating type magnetic tape, and can include a binding agent in the magnetic layer. The binding agent is one or more kinds of resin. As the binding agent, various resins normally used as a binding agent of a coating type magnetic recording medium can be used. As the binding agent, a resin selected from a polyurethane resin, a polyester resin, a polyamide resin, a vinyl chloride resin, an acrylic resin obtained by copolymerizing styrene, acrylonitrile, or methyl methacrylate, a cellulose resin such as nitrocellulose, art epoxy resin, a phenoxy resin, and a polyvinylalkylal resin such as polyvinyl acetal or polyvinyl butyral can be used alone or a plurality of resins can be mixed with each other to be used. Among these, a polyurethane resin, an acrylic resin, a cellulose resin, and a vinyl chloride resin are preferable. These resins may be a homopolymer or a copolymer. These resins can be used as the binding agent even in the non-magnetic layer and/or a back coating layer which will be described later. For the binding agent described above, descriptions disclosed in paragraphs 0028 to 0031 of JP2010-24113A can be referred to. In addition, the binding agent may be a radiation curable resin such as an electron beam curable resin. For the radiation curable resin, paragraphs 0044 and 0045 of JP2011-048878A can be referred to.

An average molecular weight of the resin used as the binding agent can be, for example, 10,000 to 200,000 as a weight-average molecular weight. The amount of the binding agent used can be, for example, 1.0 to 30.0 parts by mass with respect to 100.0 parts by mass of the ferromagnetic powder.

Curing Agent

A curing agent can also be used together with the binding agent. As the curing agent, in one aspect, a thermosetting compound which is a compound in which a curing reaction (crosslinking reaction) proceeds due to heating can be used, and in another aspect, a photocurable compound in which a curing reaction (crosslinking reaction) proceeds due to light irradiation can be used. At least a part of the curing agent is included in the magnetic layer in a state of being reacted (crosslinked) with other components such as the binding agent, by proceeding the curing reaction in the manufacturing step of the magnetic tape. The preferred curing agent is a thermosetting compound, and polyisocyanate is suitable. For the details of polyisocyanate, descriptions disclosed in paragraphs 0124 and 0125 of JP2011-216149A can be referred to. The amount of the curing agent can be, for example, 0 to 80.0 parts by mass with respect to 100.0 parts by mass of the binding agent in the magnetic layer forming composition, and is preferably 50.0 to 80.0 parts by mass, from a viewpoint of improvement of hardness of each layer such as the magnetic layer.

Other Components

The magnetic layer may include one or more kinds of additives, as necessary. As the additives, a commercially available product can be suitably selected and used according to the desired properties. Alternatively, a compound synthesized by a well-known method can be used as the additives. As the additives, the curing agent described above is used as an example. In addition, examples of the additive included in the magnetic layer include a non-magnetic filler, a lubricant, a dispersing agent, a dispersing assistant, an antibacterial agent, an antistatic agent, and an antioxidant. The non-magnetic filler is identical to the non-magnetic particles or non-magnetic powder. As the non-magnetic filler, a non-magnetic filler which can function as a projection formation agent and a non-magnetic filler which can function as an abrasive can be used. As the additive, a well-known additive such as various polymers disclosed in paragraphs 0030 to 0080 of JP2016-051493A can also be used.

As the projection formation agent which is one aspect of the non-magnetic filler, particles of an inorganic substance can be used, particles of an organic substance can be used, and composite particles of the inorganic substance and the organic substance can also be used. In addition, carbon black can also be used. Examples of the inorganic substance include inorganic oxide such as metal oxide, metal carbonate, metal sulfate, metal nitride, metal carbide, and metal sulfide, and inorganic oxide is preferable. In one aspect, the projection formation agent can be inorganic oxide-based particles. Here, “-based” means “-containing”. One aspect of the inorganic oxide-based particles is particles consisting of inorganic oxide. Another aspect of the inorganic oxide-based particles is composite particles of inorganic oxide and an organic substance, and as a specific example, composite particles of inorganic oxide and a polymer can be used. As such particles, for example, particles obtained by binding a polymer to a surface of the inorganic oxide particle can be used.

An average particle size of the projection formation agent can be, for example, 30 to 300 nm and is preferably 40 to 200 nm. In addition, regarding a shape of the projection formation agent, it is considered that the closer the shape of the projection formation agent particles contained in the magnetic layer is to a true sphere, the more likely the friction property tends to change due to a difference in head tilt angle. This is due to the following reasons. In a case where the head tilt angle is different, a contact state between the LTO8 head and the surface of the magnetic layer of the magnetic tape in a case of measuring the frictional force can change, and accordingly, a pressure applied to the surface of the magnetic layer due to the contact with the LTO8 head can also change. It is considered that the closer the shape of the particle is to a true sphere, the smaller an indentation resistance that exerts in a case where pressure is applied, and accordingly, the particles are likely to be affected by the change in pressure. With respect to this, it is surmised that, in a case where the shape of the particles is a shape other than the sphere, for example, a shape of a so-called deformed shape, a large indentation resistance is easily exerted, in a case where the pressure is applied, and accordingly, particles tends to be not likely to be affected by the change in pressure. In addition, it is considered that even particles having an inhomogeneous particle surface and low surface smoothness tend to be not likely to be affected by the change in pressure, because a large indentation resistance tends to exert in a case where the pressure is applied. Therefore, the inventors consider that, the usage of the projection formation agent whose particle shape is a shape other than the sphere and/or the usage of the projection formation agent having an inhomogeneous particle surface and low surface smoothness can contribute to making the frictional force of F_(45°)and the standard deviation of the frictional force F be in the ranges described above, respectively. In addition, in one embodiment, a projection formation agent having a so-called unspecified shape can be used as the projection formation agent.

The abrasive which is another aspect of the non-magnetic filler is preferably a non-magnetic powder having Mohs hardness exceeding 8 and more preferably a non-magnetic powder having Mohs hardness equal to or greater than 9. With respect to this, the Mohs hardness of the projection formation agent can be, for example, equal to or smaller than 8 or equal to or smaller than 7. A maximum value of Mohs hardness is 10 of diamond. Specific examples of the abrasive include powders of alumina (for example, Al₂O₃), silicon carbide, boron carbide (for example, B₄C), SiO₂, TiC, chromium oxide (Cr₂O₃), cerium oxide, zirconium oxide (for example, ZrO₂), iron oxide, diamond, and the like, and among these, alumina powder such as α-alumina and silicon carbide powder are preferable. In addition, an average particle size of the abrasive can be, for example, in a range of 30 to 300 nm and is preferably in a range of 50 to 200 nm.

From a viewpoint of causing the projection formation agent and the abrasive to exhibit these functions in more excellent manner, a content of the projection formation agent in the magnetic layer is preferably 0.1 to 4.0 parts by mass, more preferably 0.3 to 3.5 parts by mass, and even more preferably 0.5 to 2.5 parts by mass with respect to 100.0 parts by mass of the ferromagnetic powder. Meanwhile, a content of the abrasive in the magnetic layer is preferably 1.0 to 20.0 parts by mass, more preferably 3.0 to 15.0 parts by mass, and even more preferably 4.0 to 10.0 parts by mass, with respect to 100.0 parts by mass of the ferromagnetic powder.

As an example of the additive which can be used in the magnetic layer including the abrasive, a dispersing agent disclosed in paragraphs 0012 to 0022 of JP2013-131285A can be used as a dispersing agent for improving dispersibility of the abrasive in the magnetic layer forming composition. In addition, for the dispersing agent, a description disclosed in paragraphs 0061 and 0071 of JP2012-133837A can be referred to. The dispersing agent may be included in the non-magnetic layer. For the dispersing agent which may be included in the non-magnetic layer, a description disclosed in a paragraph 0061 of JP2012-133837A can be referred to.

In addition, as an aspect of an additive that can be contained in the magnetic layer, a compound having an ammonium salt structure of an alkyl ester anion represented by Formula 1 can be used.

(In Formula 1, R represents an alkyl group having 7 or more carbon atoms or a fluorinated alkyl group having 7 or more carbon atoms, and Z⁺ represents an ammonium cation.)

The present inventors consider that the compound described above can function as a lubricant. This will be described in detail below.

The lubricant can be broadly divided into a fluid lubricant and a boundary lubricant. The inventors consider that a compound having an ammonium salt structure of an alkyl ester anion represented by Formula 1 can function as a fluid lubricant. It is considered that the fluid lubricant can play a role of imparting lubricity to the magnetic layer by forming a liquid film on the surface of the magnetic layer by itself. It is surmised that, in order to control the frictional force F_(45°) and the standard deviation of the frictional force F, it is desirable that the fluid lubricant forms a liquid film on the surface of the magnetic layer. In addition, the more stably the surface of the magnetic layer and the LTO8 head can slide in a case of measuring the frictional force, the smaller the values of the frictional force F_(45°) and the standard deviation of the frictional force F can be. Regarding the liquid film of the fluid lubricant, from a viewpoint of enabling more stable sliding, it is considered that it is desirable to use an appropriate amount of the fluid lubricant which forms the liquid film on the surface of the magnetic layer. This is because it is surmised that, in a case where the amount of the liquid lubricant which forms the liquid film on the surface of the magnetic layer is excessive, the surface of the magnetic layer and the LTO8 head stick to each other, and the sliding stability tends to decrease. In addition, it is surmised that, in a case where the amount of the liquid lubricant which forms the liquid film on the surface of the magnetic layer is excessive, the projection formed on the surface of the magnetic layer by, for example, the non-magnetic filler is covered with the liquid film. It is considered that this can also be a factor that decreases the sliding stability.

With respect to the point described above, the compound described above has an ammonium salt structure of an alkyl ester anion represented by Formula 1. It is considered that the compound having such a structure can play an excellent role as the fluid lubricant even in a relatively small amount. Therefore, it is considered that including the compound described above in the magnetic layer leads to improving the sliding stability between the surface of the magnetic layer of the magnetic tape and the LTO8 head, and contributes to controlling the frictional force F_(45°) and the standard deviation of the frictional force F.

Hereinafter, the compound will be further described in detail.

In the invention and the specification, unless otherwise noted, groups described may have a substituent or may be unsubstituted. In addition, the “number of carbon atoms” of a group having a substituent means the number of carbon atoms not including the number of carbon atoms of the substituent, unless otherwise noted. In the present invention and the specification, examples of the substituent include an alkyl group (for example, an alkyl group having 1 to 6 carbon atoms), a hydroxy group, an alkoxy group (for example, an alkoxy group having 1 to 6 carbon atoms), a halogen atom (for example, a fluorine atom, a chlorine atom, a bromine atom, or the like), a cyano group, an amino group, a nitro group, an acyl group, a carboxy group, salt of a carboxy group, a sulfonic acid group, and salt of a sulfonic acid group.

Regarding the compound having an ammonium salt structure of the alkyl ester anion represented by the formula 1, at least a part thereof included in the magnetic layer can form a liquid film on the surface of the magnetic layer, and another part thereof can be included in the magnetic layer, move to the surface of the magnetic layer and form the liquid film during the sliding with the magnetic head. In addition, still another part thereof can be included in the non-magnetic layer which will be described later, and can move to the magnetic layer, further move to the surface of the magnetic layer, and form a liquid film. The “alkyl ester anion” can also be referred to as an “alkyl carboxylate anion”.

In Formula 1, R represents an alkyl group having 7 or more carbon atoms or a fluorinated alkyl group having 7 or more carbon atoms. The fluorinated alkyl group has a structure in which some or all of the hydrogen atoms constituting the alkyl group are substituted with a fluorine atom. The alkyl group or fluorinated alkyl group represented by R may have a linear structure, a branched structure, may be a cyclic alkyl group or fluorinated alkyl group, and preferably has a linear structure. The alkyl group or fluorinated alkyl group represented by R may have a substituent, may be unsubstituted, and is preferably unsubstituted. The alkyl group represented by R can be represented by, for example, C_(n)H_(2n+1)—. Here, n represents an integer of 7 or more. In addition, for example, the fluorinated alkyl group represented by R may have a structure in which a part or all of the hydrogen atoms constituting the alkyl group represented by C_(n)H_(2n+1)— are substituted with a fluorine atom. The alkyl group or fluorinated alkyl group represented by R has 7 or more carbon atoms, preferably 8 or more carbon atoms, more preferably 9 or more carbon atoms, further preferably 10 or more carbon atoms, still preferably 11 or more carbon atoms, still more preferably 12 or more carbon atoms, and still even more preferably 13 or more carbon atoms. The alkyl group or fluorinated alkyl group represented by R has preferably 20 or less carbon atoms, more preferably 19 or less carbon atoms, and even more preferably 18 or less carbon atoms.

In Formula 1, Z⁺ represents an ammonium cation. Specifically, the ammonium cation has the following structure. In the present invention and the present specification, “*” in the formulas that represent a part of the compound represents a bonding position between the structure of the part and the adjacent atom.

The nitrogen cation N⁺ of the ammonium cation and the oxygen anion O⁻ in Formula 1 may form a salt bridging group to form the ammonium salt structure of the alkyl ester anion represented by Formula 1. The fact that the compound having the ammonium salt structure of the alkyl ester anion represented by Formula 1 is contained in the magnetic layer can be confirmed by performing analysis with respect to the magnetic tape by X-ray photoelectron spectroscopy (electron spectroscopy for chemical analysis (ESCA)), infrared spectroscopy (IR), or the like.

In one embodiment, the ammonium cation represented by Z⁺ can be provided by, for example, the nitrogen atom of the nitrogen-containing polymer becoming a cation. The nitrogen-containing polymer means a polymer containing a nitrogen atom. In the present invention and the present specification, a term “polymer” means to include both a homopolymer and a copolymer. The nitrogen atom can be included as an atom configuring a main chain of the polymer in one aspect, and can be included as an atom constituting a side chain of the polymer in one aspect.

As one aspect of the nitrogen-containing polymer, polyalkyleneimine can be used. The polyalkyleneimine is a ring-opening polymer of alkyleneimine and is a polymer having a plurality of repeating units represented by Formula 2.

The nitrogen atom N configuring the main chain in Formula 2 can be converted to a nitrogen cation N⁺ to provide an ammonium cation represented by Z⁺ in Formula 1. Then, an ammonium salt structure can be formed with the alkyl ester anion, for example, as follows.

Hereinafter, Formula 2 will be described in more detail.

In Formula 2, R¹ and R² each independently represent a hydrogen atom or an alkyl group, and n1 represents an integer of 2 or more.

Examples of the alkyl group represented by R¹ or R² include an alkyl group having 1 to 6 carbon atoms, preferably an alkyl group having 1 to 3 carbon atoms, more preferably a methyl group or an ethyl group, and even more preferably a methyl group. The alkyl group represented by R¹ or R² is preferably an unsubstituted alkyl group. A combination of R¹ and R² in Formula 2 is a form in which one is a hydrogen atom and the other is an alkyl group, a form in which both are hydrogen atoms, and a form in which both are an alkyl group (the same or different alkyl groups), and is preferably a form in which both are hydrogen atoms. As the alkyleneimine that provides the polyalkyleneimine, a structure of the ring that has the smallest number of carbon atoms is ethyleneimine, and the main chain of the alkyleneimine (ethyleneimine) obtained by ring opening of ethyleneimine has 2 carbon atoms. Accordingly, n1 in Formula 2 is 2 or more. n1 in Formula 2 can be, for example, 10 or less, 8 or less, 6 or less, or 4 or less. The polyalkyleneimine may be a homopolymer containing only the same structure as the repeating structure represented by Formula 2, or may be a copolymer containing two or more different structures as the repeating structure represented by Formula 2. A number average molecular weight of the polyalkyleneimine that can be used to form the compound having the ammonium salt structure of the alkyl ester anion represented by Formula 1 can be, for example, equal to or greater than 200, and is preferably equal to or greater than 300, and more preferably equal to or greater than 400. In addition, the number average molecular weight of the polyalkyleneimine can be, for example, equal to or less than 10,000, and is preferably equal to or less than 5,000 and more preferably equal to or less than 2,000.

In the present invention and the present specification, the average molecular weight (weight-average molecular weight and number average molecular weight) is measured by gel permeation chromatography (GPC) and is a value obtained by performing standard polystyrene conversion. Unless otherwise noted, the average molecular weights shown in the examples which will be described below are values (polystyrene-equivalent values) obtained by standard polystyrene conversion of the values measured under the following measurement conditions using GPC.

GPC device: HLC-8220 (manufactured by Tosoh Corporation)

Guard Column: TSK guard column Super HZM-H

Column: TSK gel Super HZ 2000, TSK gel Super HZ 4000, TSK gel Super HZ-M (manufactured by Tosoh Corporation, 4.6 mm (inner diameter)×15.0 cm, three kinds of columns are linked in series)

Eluent: Tetrahydrofuran (THF), including stabilizer (2,6-di-t-butyl-4-methylphenol)

Eluent flow rate: 0.35 mL/min

Column temperature: 40° C.

Inlet temperature: 40° C.

Refractive index (RI) measurement temperature: 40° C.

Sample concentration: 0.3% by mass

Sample injection amount: 10 μL

In addition, as the other aspect of the nitrogen-containing polymer, polyallylamine can be used. The polyallylamine is a polymer of allylamine and is a polymer having a plurality of repeating units represented by Formula 3.

The nitrogen atom N configuring an amino group of a side chain in Formula 3 can be converted to a nitrogen cation N⁺ to provide an ammonium cation represented by Z⁺ in Formula 1. Then, an ammonium salt structure can be formed with the alkyl ester anion, for example, as follows.

A weight-average molecular weight of the polyallylamine that can be used to form the compound having the ammonium salt structure of the alkyl ester anion represented by Formula 1 can be, for example, equal to or greater than 200, and is preferably equal to or greater than 1,000, and more preferably equal to or greater than 1,500. In addition, the weight-average molecular weight of the polyallylamine can be, for example, equal to or less than 15,000, and is preferably equal to or less than 10,000 and more preferably equal to or less than 8,000.

The fact that the compound having a structure derived from polyalkyleneimine or polyallylamine as the compound having the ammonium salt structure of the alkyl ester anion represented by Formula 1 is included can be confirmed by analyzing the surface of the magnetic layer by a time-of-flight secondary ion mass spectrometry (TOF-SIMS) or the like.

The compound having the ammonium salt structure of the alkyl ester anion represented by Formula 1 can be salt of a nitrogen-containing polymer and one or more fatty acids selected from the group consisting of fatty acids having 7 or more carbon atoms and fluorinated fatty acids having 7 or more carbon atoms. The nitrogen-containing polymer forming salt can be one kind or two or more kinds of nitrogen-containing polymers, and can be, for example, a nitrogen-containing polymer selected from the group consisting of polyalkyleneimine and polyallylamine. The fatty acids forming the salt can be one kind or two or more kinds of fatty acids selected from the group consisting of fatty acids having 7 or more carbon atoms and fluorinated fatty acids having 7 or more carbon atoms. The fluorinated fatty acid has a structure in which some or all of the hydrogen atoms configuring the alkyl group bonded to a carboxy group COOH in the fatty acid are substituted with fluorine atoms. For example, the salt forming reaction can easily proceed by mixing the nitrogen-containing polymer and the fatty acids described above at room temperature. The room temperature is, for example, approximately 20° C. to 25° C. In one embodiment, one or more kinds of nitrogen-containing polymers and one or more kinds of the fatty acids described above are used as components of the magnetic layer forming composition, and the salt forming reaction can proceed by mixing these in the step of preparing the magnetic layer forming composition. In one embodiment, one or more kinds of nitrogen-containing polymers and one or more kinds of the fatty acids described above are mixed to form a salt before preparing the magnetic layer forming composition, and then, the magnetic layer forming composition can be prepared using this salt as a component of the magnetic layer forming composition. This point also applies to a case of forming a non-magnetic layer including a compound having an ammonium salt structure of an alkyl ester anion represented by Formula 1. For example, for the magnetic layer, 0.1 to 10.0 parts by mass of the nitrogen-containing polymer can be used and 0.5 to 8.0 parts by mass of the nitrogen-containing polymer is preferably used with respect to 100.0 parts by mass of ferromagnetic powder. The used amount of the fatty acids described above can be, for example, 0.05 to 1.0.0 parts by mass and is preferably 0.1 to 5.0 parts by mass, with respect to 100.0 parts by mass of ferromagnetic powder, in addition, for the non-magnetic layer, 0.1 to 10.0 parts by mass of the nitrogen-containing polymer can be used and 0.5 to 8.0 parts by mass of the nitrogen-containing polymer is preferably used with respect to 100.0 parts by mass of non-magnetic powder. The used amount of the fatty acids described above can be, for example, 0.05 to 10.0 parts by mass and is preferably 0.1 to 5.0 parts by mass, with respect to 100.0 parts by mass of non-magnetic powder. In a case where the nitrogen-containing polymer and the fatty acid are mixed to form an ammonium salt of the alkyl ester anion represented by Formula 1, the nitrogen atom configuring the nitrogen-containing polymer and the carboxy group of the fatty acid may be reacted to form the following structure, and a form including such structures are also included in the above compound.

Examples of the fatty acids include fatty acids having an alkyl group described above as R in Formula 1 and fluorinated fatty acids having a fluorinated alkyl group described above as R in Formula 1.

A mixing ratio of the nitrogen-containing polymer and the fatty acid used to form the compound having the ammonium salt structure of the alkyl ester anion represented by Formula 1 is preferably 10:90 to 90:10, more preferably 20:80 to 85:15, and even more preferably 30:70 to 80:20, as a mass ratio of nitrogen-containing polymer:fatty acid. In addition, the compound having the ammonium salt structure of the alkyl ester anion represented by Formula 1 that is contained in the magnetic layer is preferably 0.01 parts by mass or more, more preferably 0.1 parts by mass, even more preferably 0.5 parts by mass with respect to 100.0 parts by mass of the ferromagnetic powder. Here, a content of the compound in the magnetic layer means a total amount of the amount of the liquid film formed on the surface of the magnetic layer and the amount contained in the magnetic layer. On the other hand, it is preferable that a content of the ferromagnetic powder in the magnetic layer is high from a viewpoint of high-density recording. Therefore, from a viewpoint of high-density recording, it is preferable that a content of components other than the ferromagnetic powder is small. From this viewpoint, the content of the compound in the magnetic layer is preferably 15.0 parts by mass or less, more preferably 10.0 parts by mass or less, and even more preferably 8.0 parts by mass or less with respect to 100.0 parts by mass of the ferromagnetic powder. In addition, the same applies to the preferable range of the content of the compound in the magnetic layer forming composition used for forming the magnetic layer.

As the lubricant, for example, a fatty acid amide that can function as a boundary lubricant can be used. It is considered that the boundary lubricant is a lubricant which can be adsorbed to a surface of powder (for example, ferromagnetic powder) and form a rigid lubricant film to decrease contact friction. Examples of fatty acid amide include amide of various fatty acids such as lauric acid, myristic acid, palmitic acid, stearic acid, oleic acid, linoleic acid, linolenic acid, behenic acid, erucic acid, and elaidic acid, and specifically, lauric acid amide, myristic acid amide, palmitic acid amide, stearic acid amide, and the like. The content of fatty acid amide in the magnetic layer is, for example, 0 to 3.0 parts by mass, preferably 0 to 2.0 parts by mass, and more preferably 0 to 1.0 parts by mass with respect to 100.0 parts by mass of the ferromagnetic powder. In addition, the non-magnetic layer may also contain fatty acid amide. The content of fatty acid amide in the non-magnetic layer is, for example, 0 to 3.0 parts by mass and is preferably 0 to 1.0 parts by mass with respect to 100.0 parts by mass of non-magnetic powder. For the dispersing agent, a description disclosed in paragraphs 0061 and 0071 of JP2012-133837A can be referred to. The dispersing agent may be added to a non-magnetic layer forming composition. For the dispersing agent which can be added to the non-magnetic layer forming composition, a description disclosed in paragraph 0061 of JP2012-133837A can be referred to.

Non-Magnetic Layer

Next, the non-magnetic layer will be described. The magnetic tape may include a magnetic layer directly on the non-magnetic support or may include a non-magnetic layer containing the non-magnetic powder between the non-magnetic support and the magnetic layer. The non-magnetic powder used for the non-magnetic layer may be a powder of an inorganic substance (inorganic powder) or a powder of an organic substance (organic powder). In addition, carbon black and the like can be used. Examples of the inorganic substance include metal, metal oxide, metal carbonate, metal sulfate, metal nitride, metal carbide, and metal sulfide. The non-magnetic powder can be purchased as a commercially available product or can be manufactured by a well-known method. For details thereof, descriptions disclosed in paragraphs 0146 to 01.50 of JP:2011-216149A can be referred to. For carbon black which can be used in the non-magnetic layer, descriptions disclosed in paragraphs 0040 and 0041 of JP2010-24113A can be referred to. The content (filling percentage) of the non-magnetic powder of the non-magnetic layer is preferably in a range of 50% to 90% by mass and more preferably in a range of 60% to 90% by mass with respect to a total mass of the non-magnetic layer.

The non-magnetic layer can include a binding agent and can also include additives. In regards to other details of a binding agent or additives of the non-magnetic layer, the well-known technology regarding the non-magnetic layer can be applied. In addition, in regards to the type and the content of the binding agent, and the type and the content of the additive, for example, the well-known technology regarding the magnetic layer can be applied.

The non-magnetic layer of the magnetic tape also includes a substantially non-magnetic layer containing a small amount of ferromagnetic powder as impurities, or intentionally, together with the non-magnetic powder. Here, the substantially non-magnetic layer is a layer having a residual magnetic flux density equal to or smaller than 10 mT, a layer having coercivity equal to or smaller than 7.96 kA/m (100 Oe), or a layer having a residual magnetic flux density equal to or smaller than 10 mT and coercivity equal to or smaller than 7.96 kA/m (100 Oe). It is preferable that the non-magnetic layer does not have a residual magnetic flux density and coercivity.

Non-Magnetic Support

Next, the non-magnetic support will be described. As the non-magnetic support (hereinafter, also simply referred to as a “support”), well-known components such as polyethylene terephthalate, polyethylene naphthalate, polyamide, polyamide imide, aromatic polyamide subjected to biaxial stretching are used. Among these, polyethylene terephthalate, polyethylene naphthalate, and polyamide are preferable. Corona discharge, plasma treatment, easy-bonding treatment, or heat treatment may be performed with respect to these supports in advance.

Back Coating Layer

The tape may or may not include a back coating layer containing a non-magnetic powder on a surface side of the non-magnetic support opposite to the surface side provided with the magnetic layer. The back coating layer preferably includes any one or both of carbon black and inorganic powder. The back coating layer can include a binding agent and can also include additives. For the details of the non-magnetic powder, the binding agent included in the back coating layer and various additives, a well-known technology regarding the back coating layer can be applied, and a well-known technology regarding the magnetic layer and/or the non-magnetic layer can also be applied. For example, for the back coating layer, descriptions disclosed in paragraphs 0018 to 0020 of JP2006-331625A and page 4, line 65, to page 5, line 38, of U.S. Pat. No. 7,029,774B can be referred to.

Various Thicknesses

The tape thickness of the magnetic tape is as described above.

A thickness of the non-magnetic support is preferably 3.0 to 5.0 μm.

A thickness of the magnetic layer can be optimized according to a saturation magnetization amount of a magnetic head used, a head gap length, a recording signal band, and the like, is normally 0.01 μm to 0.15 μm, and is preferably 0.02 μm to 0.12 μm and more preferably 0.03 μm to 0.1 μm, from a viewpoint of realization of high-density recording. The magnetic layer may be at least single layer, the magnetic layer may be separated into two or more layers having different magnetic properties, and a configuration of a well-known multilayered magnetic layer can be applied. A thickness of the magnetic layer in a case where the magnetic layer is separated into two or more layers is the total thickness of the layers.

A thickness of the non-magnetic layer is, for example, 0.1 to 1.5 μm, preferably 0.1 to 1.0 μm, and more preferably 0.1 to 0.7 μm.

A thickness of the back coating layer is preferably equal to or smaller than 0.9 μm and more preferably 0.1 to 0.7 μm.

Various thicknesses such as the thickness of the magnetic layer and the like can be obtained by the following method.

A cross section of the magnetic tape in the thickness direction is exposed with an ion beam and the cross section observation of the exposed cross section is performed using a scanning electron microscope or a transmission electron microscope. Various thicknesses can be obtained as the arithmetic mean of the thicknesses obtained at two random portions in the cross section observation. Alternatively, various thicknesses can be obtained as a designed thickness calculated under the manufacturing conditions.

Manufacturing Method

Preparation of Each Layer Forming Composition

Composition for forming the magnetic layer, the non-magnetic layer, or the back coating layer generally includes a solvent, together with the various components described above. As the solvent, various organic solvents generally used for manufacturing a coating type magnetic recording medium can be used. Among them, from a viewpoint of the solubility of the binding agent usually used for the coating type magnetic recording medium, each layer forming composition preferably contains one or more of a ketone solvent such as acetone, methyl ethyl ketone, methyl isobutyl ketone, diisobutyl ketone, cyclohexanone, isophorone, and tetrahydrofuran. The amount of solvent in each layer forming composition is not particularly limited, and can be identical to that in each layer forming composition of a typical coating type magnetic recording medium. In addition, a step of preparing each layer forming composition can generally include at least a kneading step, a dispersing step, and a mixing step provided before and after these steps, as necessary. Each step may be divided into two or more stages. The component used in the preparation of each layer forming composition may be added at an initial stage or in a middle stage of each step. Each component may be separately added in two or more steps. For example, a binding agent may be separately added in a kneading step, a dispersing step, and a mixing step for adjusting viscosity after the dispersion. In addition, as described above, one or more kinds of nitrogen-containing polymers and one or more kinds of the fatty acids described above are used as components of the magnetic layer forming composition, and the salt forming reaction can proceed by mixing these in the step of preparing the magnetic layer forming composition. In one embodiment, one or more kinds of nitrogen-containing polymers and one or more kinds of the fatty acids described above are mixed to form a salt before preparing the magnetic layer forming composition, and then, the magnetic layer forming composition can be prepared using this salt as a component of the magnetic layer forming composition. This point also applies to a step of preparing the non-magnetic layer forming composition. In one aspect, in the step of preparing the magnetic layer forming composition, a dispersion liquid including a projection formation agent (hereinafter, referred to as a “projection formation agent liquid”) can be prepared, and then this projection formation agent liquid can be mixed with one or more other components of the magnetic layer forming composition. For example, the projection formation agent liquid can be prepared by a well-known dispersion process such as ultrasonic treatment. The ultrasonic treatment can be performed, for example, for about 1 to 300 minutes at an ultrasonic output of about 10 to 2,000 watts per 200 cc (1 cc=1 cm³). In addition, the filtering may be performed after a dispersion process. For the filter used for the filtering, the following description can be referred to.

In the manufacturing step of the magnetic tape, a well-known manufacturing technology of the related art can be used as a part of step or the entire step. In the kneading step, an open kneader, a continuous kneader, a pressure kneader, or a kneader having a strong kneading force such as an extruder is preferably used. For details of the kneading processes, descriptions disclosed in JP1989-106338A (JP-H01-106338A) and JP1989-79274A (JP-H01-79274A) can be referred to. In addition, glass beads and/or other beads can be used to disperse each layer forming composition. As such dispersion beads, zirconia beads, titania beads, and steel beads which are dispersion beads having high specific gravity are suitable. These dispersion beads is preferably used by optimizing a particle diameter (bead diameter) and a filling percentage of these dispersion beads. As a disperser, a well-known dispersion device can be used. Each layer forming composition may be filtered by a well-known method before performing the coating step. The filtering can be performed by using a filter, for example. As the filter used in the filtering, a filter having a hole diameter of 0.01 to 3 μm (for example, filter made of glass fiber or filter made of polypropylene) can be used, for example.

Coating Step

The magnetic layer can be formed, for example, by directly applying the magnetic layer forming composition onto the non-magnetic support or performing multilayer coating of the magnetic layer forming composition with the non-magnetic layer forming composition in order or at the same time. In an case of performing an alignment process, while the coating layer of the magnetic layer forming composition is wet, the alignment, process is performed with respect to the coating layer in an alignment zone. For the alignment process, various technologies disclosed in a paragraph 0052 of JP2010-24113A can be applied. For example, a homeotropic alignment process can be performed by a well-known method such as a method using a different polar facing magnet. In the alignment zone, a drying speed of the coating layer can be controlled by a temperature and an air flow of the dry air and/or a transporting rate in the alignment zone. In addition, the coating layer may be preliminarily dried before transporting to the alignment zone.

The back coating layer can be formed by applying a back coating layer forming composition onto a side of the non-magnetic support opposite to the side provided with the magnetic layer (or to be provided with the magnetic layer). For details of the coating for forming each layer, a description disclosed in a paragraph 0066 of JP2010-231843A can be referred to.

Other Steps

After performing the coating step described above, a calendar process is usually performed in order to improve surface smoothness of the magnetic tape. For calendar conditions, a calendar pressure is, for example, 200 to 500 kN/m and preferably 250 to 350 kN/m, a calendar temperature (surface temperature of calendar roll) is, for example, 70° C. to 120° C. and preferably 80° C. to 100° C., and a calendar speed is, for example, 50 to 300 m/min and preferably 80 to 200 m/min. In addition, as a roll having a hard surface is used as a calendar roll, or as the number of stages is increased, the surface of the magnetic layer tends to be smoother.

For various other steps for manufacturing a magnetic tape, a description disclosed in paragraphs 0067 to 0070 of JP2010-231843A can be referred to.

Through various steps, a long magnetic tape raw material can be obtained. The obtained magnetic tape raw material is, for example, cut (slit) by a well-known cutter to have a width of a magnetic tape to be accommodated in the magnetic tape cartridge. The width can be determined according to the standard and is normally ½ inches.

In the magnetic tape obtained by slitting, normally, a servo pattern can be formed.

Heat Treatment

In one embodiment, the magnetic tape can be a magnetic tape manufactured through the following heat treatment. In another aspect, the magnetic tape can be manufactured without the following heat treatment.

The heat treatment can be performed in a state where the magnetic tape slit and have a width determined according to the standard is wound around a core member.

In one embodiment, the heat treatment is performed in a state where the magnetic tape is wound around the core member for heat treatment (hereinafter, referred to as a “core for heat treatment”), the magnetic tape after the heat treatment is wound around a cartridge reel of the magnetic tape cartridge, and a magnetic tape cartridge in which the magnetic tape is wound around the cartridge reel can be manufactured.

The core for heat treatment can be formed of metal, a resin, or paper. The material of the core for heat treatment is preferably a material having high stiffness, from a viewpoint of preventing the occurrence of a winding defect such as spoking or the like. From this viewpoint, the core for heat treatment is preferably formed of metal or a resin. In addition, as an index for stiffness, a bending elastic modulus of the material for the core for heat treatment is preferably equal to or greater than 0.2. GPa (gigapascal) and more preferably equal to or greater than 0.3 GPa. Meanwhile, since the material having high stiffness is normally expensive, the use of the core for heat treatment of the material having stiffness exceeding the stiffness capable of preventing the occurrence of the winding defect causes the cost increase. By considering the viewpoint described above, the bending elastic modulus of the material for the core for heat treatment is preferably equal to or smaller than 250 GPa. The bending elastic modulus is a value measured based on international organization for standardization (ISO) 178 and the bending elastic modulus of various materials is well known. In addition, the core for heat treatment can be a solid or hollow core member. In a case of a hollow shape, a wall thickness is preferably equal to or greater than 2 mm, from a viewpoint of maintaining the stiffness. In addition, the core for heat treatment may include or may not include a flange.

The magnetic tape having a length equal to or greater than a length to be finally accommodated in the magnetic tape cartridge (hereinafter, referred to as a “final product length”) is prepared as the magnetic tape wound around the core for heat treatment, and it is preferable to perform the heat treatment by placing the magnetic tape in the heat treatment environment, in a state where the magnetic tape is wound around the core for heat treatment. The magnetic tape length wound around the core for heat treatment is equal to or greater than the final product length, and is preferably the “final product length+α”, from a viewpoint of ease of winding around the core for heat treatment. This α is preferably equal to or greater than 5 m, from a viewpoint of ease of the winding. The tension in a case of winding around the core for heat treatment is preferably equal to or greater than 0.1 N (newton). In addition, from a viewpoint of preventing the occurrence of excessive deformation during the manufacturing, the tension in a case of winding around the core for heat treatment is preferably equal to or smaller than 1.5 N and more preferably equal to or smaller than 1.0 N. An outer diameter of the core for heat treatment is preferably equal to or greater than 20 mm and more preferably equal to or greater than 40 mm, from viewpoints of ease of the winding and preventing coiling (curl in longitudinal direction). The outer diameter of the core for heat treatment is preferably equal to or smaller than 100 mm and more preferably equal to or smaller than 90 mm A width of the core for heat treatment may be equal to or greater than the width of the magnetic tape wound around this core. In addition, after the heat treatment, in a case of detaching the magnetic tape from the core for heat treatment, it is preferable that the magnetic tape and the core for heat treatment are sufficiently cooled and magnetic tape is detached from the core for heat treatment, in order to prevent the occurrence of the tape deformation which is not intended during the detaching operation. It is preferable the detached magnetic tape is wound around another core temporarily (referred to as a “core for temporary winding”), and the magnetic tape is wound around a cartridge reel (generally, outer diameter is approximately 40 to 50 mm) of the magnetic tape cartridge from the core for temporary winding. Accordingly, a relationship between the inside and the outside with respect to the core for heat treatment of the magnetic tape in a case of the heat treatment can be maintained and the magnetic tape can be wound around the cartridge reel of the magnetic tape cartridge. Regarding the details of the core for temporary winding and the tension in a case of winding the magnetic tape around the core, the description described above regarding the core for heat treatment can be referred to. In an aspect in which the heat treatment is subjected to the magnetic tape having a length of the “final product length+α”, the length corresponding to “+α” may be cut in any stage. For example, in one aspect, the magnetic tape having the final product length may be wound around the reel of the magnetic tape cartridge from the core for temporary winding and the remaining length corresponding the “+α” may be cut. From a viewpoint of decreasing the amount of the portion to be cut out and removed, the α is preferably equal to or smaller than 20 m.

The specific aspect of the heat treatment performed in a state of being wound around the core member as described above is described below.

An atmosphere temperature for performing the heat treatment (hereinafter, referred to as a “heat treatment temperature”) is preferably equal to or higher than 40° C. and more preferably equal to or higher than 50° C. the other hand, from a viewpoint of preventing the excessive deformation, the heat treatment temperature is preferably equal to or lower than 75° C. and more preferably equal to or lower than 70° C.

A weight absolute humidity of the atmosphere for performing the heat treatment is preferably equal to or greater than 0.1 g/kg Dry air and more preferably equal to or greater than 1 g/kg Dry air. The atmosphere in which the weight absolute humidity is in the range described above is preferable, because it can be prepared without using a special device for decreasing moisture. On the other hand, the weight absolute humidity is preferably equal to or smaller than 70 g/kg Dry air and more preferably equal to or smaller than 66 g/kg Dry air, from a viewpoint of preventing a deterioration in workability by dew condensation. The heat treatment time is preferably equal to or longer than 0.3 hours and more preferably equal to or longer than 0.5 hours. In addition, the heat treatment time is preferably equal to or shorter than 48 hours, from a viewpoint of production efficiency.

Regarding the control of the standard deviation of the curvature described above, as any value of the heat treatment temperature, heat treatment time, modulus of bending elasticity of a core for the heat treatment, and tension at the time of winding around the core for the heat treatment is large, the value of the curvature tends to further decrease.

Formation of Servo Pattern

The “formation of the servo pattern” can be “recording of a servo signal”. The formation of the servo pattern will be described below.

The servo pattern is generally formed along a longitudinal direction of the magnetic tape. As a system of control using a servo signal (servo control), timing-based servo (TBS), amplitude servo, or frequency servo is used.

As shown in European Computer Manufacturers Association (ECMA)-319 (June 2001), a timing-based servo system is used in a magnetic tape based on a linear tape-open (LTO) standard (generally referred to as an “LTO tape”). In this timing-based servo system, the servo pattern is configured by continuously disposing a plurality of pairs of magnetic stripes (also referred to as “servo stripes”) not parallel to each other in a longitudinal direction of the magnetic tape. In the invention and the specification, the “timing-based servo pattern” refers to a servo pattern that enables head tracking in a servo system of a timing-based servo system. As described above, a reason for that the servo pattern is configured with one pair of magnetic stripes not parallel to each other is because a servo signal reading element passing on the servo pattern recognizes a passage position thereof. Specifically, one pair of the magnetic stripes are formed so that a gap thereof is continuously changed along the width direction of the magnetic tape, and a relative position of the servo pattern and the servo signal reading element can be recognized, by the reading of the gap thereof by the servo signal reading element. The information of this relative position can realize the tracking of a data track. Accordingly, a plurality of servo tracks are generally set on the servo pattern along the width direction of the magnetic tape.

The servo band is configured of servo patterns continuous in the longitudinal direction of the magnetic tape. A plurality of servo bands are normally provided on the magnetic tape, For example, the number thereof is 5 in the LTO tape. A region interposed between two adjacent servo bands is a data band. The data band is configured of a plurality of data tracks and each data track corresponds to each servo track.

In one aspect, as shown in JP2004-318983A, information showing the number of servo band (also referred to as “servo band identification (ID)” or “Unique Data Band Identification Method (UDIM) information”) is embedded in each servo band. This servo band ID is recorded by shifting a specific servo stripe among the plurality of pair of servo stripes in the servo band so that the position thereof is relatively deviated in the longitudinal direction of the magnetic tape. Specifically, the position of the shifted specific servo stripe among the plurality of pair of servo stripes is changed for each servo band. Accordingly, the recorded servo band ID becomes unique for each servo band, and therefore, the servo hand can be uniquely specified by only reading one servo band by the servo signal reading element.

In a method of uniquely specifying the servo band, a staggered method as shown in ECMA-319 (June 2001) is used. In this staggered method, a plurality of the groups of one pair of magnetic stripes (servo stripe) not parallel to each other which are continuously disposed in the longitudinal direction of the magnetic tape is recorded so as to be shifted in the longitudinal direction of the magnetic tape for each servo band. A combination of this shifted servo hand between the adjacent servo bands is set to be unique in the entire magnetic tape, and accordingly, the servo band can also be uniquely specified by reading of the servo pattern by two servo signal reading elements.

In addition, as shown in ECMA-319 (June 2001), information showing the position in the longitudinal direction of the magnetic tape (also referred to as “Longitudinal Position (LPOS) information”) is normally embedded in each servo band. This LPOS information is recorded so that the position of one pair of servo stripes is shifted in the longitudinal direction of the magnetic tape, in the same manner as the UDIM information. However, unlike the UDIM information, the same signal is recorded on each servo band in this LPOS information.

Other information different from the UDIM information and the LPOS information can be embedded in the servo band. In this case, the embedded information may be different for each servo band as the UDIM information, or may be common in all of the servo bands, as the LPOS information.

In addition, as a method of embedding the information in the servo band, a method other than the method described above can be used. For example, a predetermined code may be recorded by thinning out a predetermined pair among the group of pairs of the servo stripes.

A servo pattern forming head is also referred to as a servo write head. The servo write head generally includes pairs of gaps corresponding to the pairs of magnetic stripes by the number of servo hands. In general, a core and a coil are respectively connected to each of the pairs of gaps, and a magnetic field generated in the core can generate leakage magnetic field in the pairs of gaps, by supplying a current pulse to the coil. In a case of forming the servo pattern, by inputting a current pulse while causing the magnetic tape to run on the servo write head, the magnetic pattern corresponding to the pair of gaps is transferred to the magnetic tape, and the servo pattern can be formed. A width of each gap can be suitably set in accordance with a density of the servo pattern to be formed. The width of each gap can be set as, for example, equal to or smaller than 1 μm, 1 to 10 μm, or equal to or greater than 10 μm.

Before forming the servo pattern on the magnetic tape, a demagnetization (erasing) process is generally performed on the magnetic tape. This erasing process can be performed by applying a uniform magnetic field to the magnetic tape by using a DC magnet and an AC magnet. The erasing process includes direct current (DC) erasing and alternating current (AC) erasing. The AC erasing is performed by slowing decreasing an intensity of the magnetic field, while reversing a direction of the magnetic field applied to the magnetic tape. Meanwhile, the DC erasing is performed by applying the magnetic field in one direction to the magnetic tape. The DC erasing further includes two methods. A first method is horizontal DC erasing of applying the magnetic field in one direction along a longitudinal direction of the magnetic tape. A second method is vertical DC erasing of applying the magnetic field in one direction along a thickness direction of the magnetic tape. The erasing process may be performed with respect to all of the magnetic tape or may be performed for each servo band of the magnetic tape.

A direction of the magnetic field to the servo pattern to be formed is determined in accordance with the direction of erasing. For example, in a case where the horizontal DC erasing is performed to the magnetic tape, the formation of the servo pattern is performed so that the direction of the magnetic field and the direction of erasing is opposite to each other. Accordingly, the output of the servo signal obtained by the reading of the servo pattern can be increased. As disclosed in JP2012-53940A, in a case where the magnetic pattern is transferred to the magnetic tape subjected to the vertical DC erasing by using the gap, the servo signal obtained by the reading of the formed servo pattern has a unipolar pulse shape. Meanwhile, in a case where the magnetic pattern is transferred to the magnetic tape subjected to the horizontal DC erasing by using the gap, the servo signal obtained by the reading of the formed servo pattern has a bipolar pulse shape.

<Vertical Squareness Ratio>

In one embodiment, the vertical squareness ratio of the magnetic tape can be, for example, 0.55 or more. From a viewpoint of improving the electromagnetic conversion characteristics, the vertical squareness ratio of the magnetic tape is preferably 0.60 or more, and more preferably 0.65 or more. In principle, an upper limit of the squareness ratio is 1.00 or less. The vertical squareness ratio of the magnetic tape can be 1.00 or less, 0.95 or less, 0.90 or less, 0.85 or less, or 0.80 or less. It is preferable that the value of the vertical squareness ratio of the magnetic tape is large from a viewpoint of improving the electromagnetic conversion characteristics. The vertical squareness ratio of the magnetic tape can be controlled by a well-known method such as performing a homeotropic alignment process.

In the invention and the specification, the “vertical squareness ratio” is squareness ratio measured in the vertical direction of the magnetic tape. The “vertical direction” described with respect to the squareness ratio is a direction orthogonal to the surface of the magnetic layer, and can also be referred to as a thickness direction. In the invention and the specification, the vertical squareness ratio is obtained by the following method.

A sample piece having a size that can be introduced into an oscillation sample type magnetic-flux meter is cut out from the magnetic tape to be measured. Regarding the sample piece, using the oscillation sample type magnetic-flux meter, a magnetic field is applied to a vertical direction of a sample piece (direction orthogonal to the surface of the magnetic layer) with a maximum applied magnetic field of 3979 kA/m, a measurement temperature of 296 K, and a magnetic field sweep speed of 8.3 kA/m/sec, and a magnetization strength of the sample piece with respect to the applied magnetic field is measured. The measured value of the magnetization strength is obtained as a value after diamagnetic field correction and a value obtained by subtracting magnetization of a sample probe of the oscillation sample type magnetic-flux meter as background noise. In a case where the magnetization strength at the maximum applied magnetic field is Ms and the magnetization strength at zero applied magnetic field is Mr, the squareness ratio SQ s a value calculated as SQ=Mr/Ms. The measurement temperature is referred to as a temperature of the sample piece, and by setting the ambient temperature around the sample piece to a measurement temperature, the temperature of the sample piece can be set to the measurement temperature by realizing temperature equilibrium.

Magnetic Tape Cartridge

According to another aspect of the present invention, there is provided a magnetic tape cartridge including the magnetic tape described above.

The details of the magnetic tape included in the magnetic tape cartridge are as described above.

In the magnetic tape cartridge, the magnetic tape is generally accommodated in a cartridge main body in a state of being wound around a reel. The reel is rotatably provided in the cartridge main body. As the magnetic tape cartridge, a single reel type magnetic tape cartridge including one reel in a cartridge main body and a twin reel type magnetic tape cartridge including two reels in a cartridge main body are widely used. In a case where the single reel type magnetic tape cartridge is mounted in the magnetic tape device in order to record and/or reproduce data on the magnetic tape, the magnetic tape is drawn from the magnetic tape cartridge and wound around the reel on the magnetic tape device side. A magnetic head is disposed on a magnetic tape transportation path from the magnetic tape cartridge to a winding reel. Feeding and winding of the magnetic tape are performed between a reel (supply reel) on the magnetic tape cartridge side and a reel (winding reel) on the magnetic tape device side. In the meantime, the magnetic head comes into contact with and slides on the surface of the magnetic layer of the magnetic tape, and accordingly, the recording and/or reproducing of data is performed. With respect to this, in the twin reel type magnetic tape cartridge, both reels of the supply reel and the winding reel are provided in the magnetic tape cartridge.

In one aspect, the magnetic tape cartridge can include a cartridge memory. The cartridge memory can be, for example, a non-volatile memory, and head tilt angle adjustment information is recorded in advance or head tilt angle adjustment information is recorded. The head tilt angle adjustment information is information for adjusting the head tilt angle during the running of the magnetic tape in the magnetic tape device. For example, as the head tilt angle adjustment information, a value of the servo band spacing at each position in the longitudinal direction of the magnetic tape at the time of data recording can be recorded. For example, in a case where the data recorded on the magnetic tape is reproduced, the value of the servo band spacing is measured at the time of the reproducing, and the head tilt angle can be changed by the control device of the magnetic tape device so that an absolute value of a difference of the servo band spacing at the time of recording at the same longitudinal position recorded in the cartridge memory is close to 0. The head tilt angle can be, for example, the angle θ described above.

The magnetic tape and the magnetic tape cartridge can be suitably used in the magnetic tape device (that is, magnetic recording and reproducing system) for performing recording and/or reproducing data at different head tilt angles. In such a magnetic tape device, in one embodiment, it is possible to perform the recording and/or reproducing of data by changing the head tilt angle during running of a magnetic tape. For example, the head tilt angle can be changed according to dimensional information of the magnetic tape in the width direction obtained while the magnetic tape is running. In addition, for example, in a usage aspect, a head tilt angle during the recording and/or reproducing at a certain time and a head tilt angle during the recording and/or reproducing at the next time and subsequent times are changed, and then the head tilt angle may be fixed without changing during the running of the magnetic tape for the recording and/or reproducing of each time. In any usage aspect, a magnetic tape having high running stability in a case of performing the recording and/or reproducing of data at different head tilt angles is preferable.

Magnetic Tape Device

One aspect of the invention relates to a magnetic tape device including the magnetic tape described above. In the magnetic tape device, the recording of data on the magnetic tape and/or the reproducing of data recorded on the magnetic tape can be performed by bringing the surface of the magnetic layer of the magnetic tape into contact with the magnetic head and sliding. The magnetic tape device can attachably and detachably include the magnetic tape cartridge according to one aspect of the invention.

The magnetic tape cartridge can be attached to a magnetic tape device provided with a magnetic head and used for performing the recording and/or reproducing of data. In the invention and the specification, the “magnetic tape device” means a device capable of performing at least one of the recording of data on the magnetic tape or the reproducing of data recorded on the magnetic tape. Such a device is generally called a drive.

Magnetic Head

The magnetic tape device can include a magnetic head. The configuration of the magnetic head and the angle θ, which is the head tilt angle, are as described above with reference to FIGS. 1 to 3 . The magnetic head included in the magnetic tape device can be an LTO8 head in one aspect, an LTO head of another generation in another aspect, and a magnetic head other than the LTO head in still another aspect. In a case where the magnetic head includes a reproducing element, as the reproducing element, a magnetoresistive (MR) element capable of reading information recorded on the magnetic tape with excellent sensitivity is preferable. As the MR element, various well-known MR elements (for example, a Giant Magnetoresistive (GMR) element, or a Tunnel Magnetoresistive (TMR) element) can be used. Hereinafter, the magnetic head which records data and/or reproduces the recorded data is also referred to as a “recording and reproducing head”. The element for recording data (recording element) and the element for reproducing data (reproducing element) are collectively referred to as a “magnetic head element”.

By reproducing data using the reproducing element having a narrow reproducing element width as the reproducing element, the data recorded at high density can be reproduced with high sensitivity. From this viewpoint, the reproducing element width of the reproducing element is preferably 0.8 μm or less. The reproducing element width of the reproducing element can be, for example, 0.3 μm or more. However, it is also preferable to fall below this value from the above viewpoint.

Here, the “reproducing element width” refers to a physical dimension of the reproducing element width. Such physical dimensions can be measured with an optical microscope, a scanning electron microscope, or the like.

In a case of recording data and/or reproducing recorded data, first, tracking using a servo signal can be performed. That is, as the servo signal reading element follows a predetermined servo track, the magnetic head element can be controlled to pass on the target data track. The movement of the data track is performed by changing the servo track to be read by the servo signal reading element in the tape width direction.

In addition, the recording and reproducing head can perform the recording and/or reproducing with respect to other data bands. In this case, the servo signal reading element is moved to a predetermined servo band by using the UDIM information described above, and the tracking with respect to the servo band may be started.

FIG. 5 shows an example of disposition of data bands and servo bands. In FIG. 5 , a plurality of servo bands 1 are disposed to be interposed between guide bands 3 in a magnetic layer of a magnetic tape MT. A plurality of regions 2 each of which is interposed between two servo bands are data bands. The servo pattern is a magnetized region and is formed by magnetizing a specific region of the magnetic layer by a servo write head. The region magnetized by the servo write head (position where a servo pattern is formed) is determined by standards. For example, in an LTO Ultrium format tape which is based on a local standard, a plurality of servo patterns tilted in a tape width direction as shown in FIG. 6 are formed on a servo band, in a case of manufacturing a magnetic tape. Specifically, in FIG. 6 , a servo frame SF on the servo band 1 is configured with a servo sub-frame 1 (SSF1) and a servo sub-frame 2 (SSF2). The servo sub-frame 1 is configured with an A burst (in FIG. 6 , reference numeral A) and a B burst (in FIG. 6 , reference numeral B). The A burst is configured with servo patterns A1 to A5 and the B burst is configured with servo patterns B1 to B5. Meanwhile, the servo sub-frame 2 is configured with a C burst (in FIG. 6 , reference numeral C) and a D burst (in FIG. 6 , reference numeral D). The C burst is configured with servo patterns C1 to C4 and the D burst is configured with servo patterns D1 to D4. Such 18 servo patterns are disposed in the sub-frames in the arrangement of 5, 5, 4, 4, as the sets of 5 servo patterns and 4 servo patterns, and are used for recognizing the servo frames. FIG. 6 shows one servo frame for explaining. However, in practice, in the magnetic layer of the magnetic tape in which the head tracking servo in the timing-based servo system is performed, a plurality of servo frames are disposed in each servo band in a running direction. In FIG. 6 , an arrow shows a magnetic tape running direction. For example, an LTO Ultrium format tape generally includes 5,000 or more servo frames per a tape length of 1 m, in each servo band of the magnetic layer.

In the magnetic tape device, the head tilt angle can be changed while the magnetic tape is running in the magnetic tape device. The head tilt angle is, for example, an angle θ formed by the axis of the element array with respect to the width direction of the magnetic tape. The angle θ is as described above. For example, by providing an angle adjustment unit for adjusting the angle of the module of the magnetic head in the recording and reproducing head unit of the magnetic head, the angle θ can be variably adjusted during the running of the magnetic tape. Such an angle adjustment unit can include, for example, a rotation mechanism for rotating the module. For the angle adjustment unit, a well-known technology can be applied.

Regarding the head tilt angle during the running of the magnetic tape, in a case where the magnetic head includes a plurality of modules, the angle θ described with reference to FIGS. 1 to 3 can be specified for the randomly selected module. The angle θ at the start of running of the magnetic tape, θ_(initial), can be set to 0° or more or more than 0°. As the θ_(initial) is large, a change amount of the distance between the servo signal reading elements with respect to a change amount of the angle θ increases, and accordingly, it is preferable from a viewpoint of adjustment ability for adjusting the distance between the servo signal reading elements according to the dimension change of the width direction of the magnetic tape. From this viewpoint, the θ_(initial) is preferably 1° or more, more preferably 5° or more, and even more preferably 10° or more. Meanwhile, regarding an angle (generally referred to as a “lap angle”) formed by a surface of the magnetic layer and a contact surface of the magnetic head in a case where the magnetic tape runs and comes into contact with the magnetic head, a deviation in a tape width direction which is kept small is effective in improving uniformity of friction in the tape width direction which is generated by the contact between the magnetic head and the magnetic tape during the running of the magnetic tape. In addition, it is desirable to improve the uniformity of the friction in the tape width direction from a viewpoint of position followability and the running stability of the magnetic head. From a viewpoint of reducing the deviation of the lap angle in the tape width direction, θ_(initial) is preferably 45° or less, more preferably 40° or less, and even more preferably 35° or less.

Regarding the change of the angle θ during the running of the magnetic tape, while the magnetic tape is running in the magnetic tape device in order to record data on the magnetic tape and/or to reproduce data recorded on the magnetic tape, in a case where the angle θ of the magnetic head changes from θ_(initial) at the start of running, a maximum change amount Δθ of the angle θ during the running of the magnetic tape is a larger value among Δθ_(max) and Δθ_(min) calculated by the following equation. A maximum value of the angle θ during the running of the magnetic tape is θ_(max), and a minimum value thereof is θ_(min). In addition, “max” is an abbreviation for maximum, and “min” is an abbreviation for minimum.

Δθ_(max)=θ_(max)−θ_(initial) and

Δθ_(min)=θ_(initial)−θ_(min).

In one embodiment, the Δθ can be more than 0.000°, and is preferably 0.001° or more and more preferably 0.010° or more, from a viewpoint of adjustment ability for adjusting the effective distance between the servo signal reading elements according to the dimension change in the width direction of the magnetic tape. In addition, from a viewpoint of ease of ensuring synchronization of recorded data and/or reproduced data between a plurality of magnetic head elements during data recording and/or reproducing, the Δθ is preferably 1.000° or less, more preferably 0.900° or less, even more preferably 0.800° or less, still preferably 0.700° or less, and still more preferably 0.600° or less.

In the examples shown in FIGS. 2 and 3 , the axis of the element array is tilted toward a magnetic tape running direction. However, the present invention is not limited to such an example. The present invention also includes an aspect in which the axis of the element array is tilted in a direction opposite to the magnetic tape running direction in the magnetic tape device.

The head tilt angle θ_(initial) at the start of the running of the magnetic tape can be set by a control device or the like of the magnetic tape device.

Regarding the head tilt angle during the running of the magnetic tape, FIG. 7 is an explanatory diagram of a method for measuring the angle θ during the running of the magnetic tape. The angle θ during the running of the magnetic tape can be obtained, for example, by the following method. In a case where the angle θ during traveling on the magnetic tape is obtained by the following method, the angle θ is changed in a range of 0° to 90° during the running of the magnetic tape. That is, in a case where the axis of the element array is tilted toward the magnetic tape running direction at the start of running of the magnetic tape, the element array is not tilted so that the axis of the element array tilts toward a direction opposite to the magnetic tape running direction at the start of the running of the magnetic tape, during the running of the magnetic tape, and in a case where the axis of the element array is tilted toward the direction opposite to the magnetic tape running direction at the start of running of the magnetic tape, the element array is not tilted so that the axis of the element array tilts toward the magnetic tape running direction at the start of the running of the magnetic tape, during the running of the magnetic tape.

A phase difference (that is, time difference) ΔT of reproduction signals of the pair of servo signal reading elements 1 and 2 is measured. The measurement of ΔT can be performed by a measurement unit provided in the magnetic tape device. A configuration of such a measurement unit is well known. A distance L between a central portion of the servo signal reading element 1 and a central portion of the servo signal reading element 2 can be measured with an optical microscope or the like. In a case where a running speed of the magnetic tape is defined as a speed v, the distance in the magnetic tape running direction between the central portions of the two servo signal reading elements is set to L sin θ, and a relationship of L sin θ=v×ΔT is satisfied. Therefore, the angle θ during the running of the magnetic tape can be calculated by a formula “θ=arcsin (vΔT/L)”. The right drawing of FIG. 7 shows an example in which the axis of the element array is tilted toward the magnetic tape running direction. In this example, the phase difference (that is, time difference) ΔT of a phase of the reproduction signal of the servo signal reading element 2 with respect to a phase of the reproduction signal of the servo signal reading element 1 is measured. In a case where the axis of the element array is tilted toward the direction opposite to the running direction of the magnetic tape, θ can be obtained by the method described above, except for measuring ΔT as the phase difference (that is, time difference) of the phase of the reproduction signal of the servo signal reading element 1 with respect to the phase of the reproduction signal of the servo signal reading element 2.

For a measurement pitch of the angle θ, that is, a measurement interval of the angle θ in a tape longitudinal direction, a suitable pitch can be selected according to a frequency of tape width deformation in the tape longitudinal direction. As an example, the measurement pitch can be, for example, 250 μm.

Configuration of Magnetic Tape Device

A magnetic tape device 10 shown in FIG. 8 controls a recording and reproducing head unit 12 in accordance with a command from a control device 11 to record and reproduce data on a magnetic tape MT.

The magnetic tape device 10 has a configuration of detecting and adjusting a tension applied n a longitudinal direction of the magnetic tape from spindle motors 17A and 17B and driving devices 18A and 18B which rotatably control a magnetic tape cartridge reel and a winding reel.

The magnetic tape device 10 has a configuration in which the magnetic tape cartridge 13 can be mounted.

The magnetic tape device 10 includes a cartridge memory read and write device 14 capable of performing reading and writing with respect to the cartridge memory 131 in the magnetic tape cartridge 13.

An end portion or a leader pin of the magnetic tape MT is pulled out from the magnetic tape cartridge 13 mounted on the magnetic tape device 10 by an automatic loading mechanism or manually and passes on a recording and reproducing head through guide rollers 15A and 15B so that a surface of a magnetic layer of the magnetic tape MT comes into contact with a surface of the recording and reproducing head of the recording and reproducing head unit 12, and accordingly, the magnetic tape MT is wound around the winding reel 16.

The rotation and torque of the spindle motor 17A and the spindle motor 17B are controlled by a signal from the control device 11, and the magnetic tape MT runs at random speed and tension. A servo pattern previously formed on the magnetic tape can be used to control the tape speed and control the head tilt angle. A tension detection mechanism may be provided between the magnetic tape cartridge 13 and the winding reel 16 to detect the tension. The tension may be controlled by using the guide rollers 15A and 15B in addition to the control by the spindle motors 17A and 17B.

The cartridge memory read and write device 14 is configured to be able to read and write information of the cartridge memory 131 according to commands from the control device 11. As a communication system between the cartridge memory read and write device 14 and the cartridge memory 131, for example, an international organization for standardization (ISO) 14443 system can be used.

The control device 11 includes, for example, a controller, a storage unit, a communication unit, and the like.

The recording and reproducing head unit 12 is composed of, for example, a recording and reproducing head, a servo tracking actuator for adjusting a position of the recording and reproducing head in a track width direction, a recording and reproducing amplifier 19, a connector cable for connecting to the control device 11. The recording and reproducing head is composed of, for example, a recording element for recording data on a magnetic tape, a reproducing element for reproducing data of the magnetic tape, and a servo signal reading element for reading a servo signal recorded on the magnetic tape. For example, one or more of each of the recording elements, the reproducing element, and the servo signal reading element are mounted in one magnetic head. Alternatively, each element may be separately provided in a plurality of magnetic heads according to a running direction of the magnetic tape.

The recording and reproducing head unit 12 is configured to be able to record data on the magnetic tape MT according to a command from the control device 11. In addition, the data recorded on the magnetic tape MT can be reproduced according to a command from the control device 11.

The control device 11 has a mechanism of controlling the servo tracking actuator so as to obtain a running position of the magnetic tape from a servo signal read from a servo band during the running of the magnetic tape MT and position the recording element and/or the reproducing element at a target running position (track position). The control of the track position is performed by feedback control, for example. The control device 11 has a mechanism of obtaining a servo band spacing from servo signals read from two adjacent servo bands during the running of the magnetic tape MT. The control device 11 can store the obtained information of the servo band spacing in the storage unit inside the control device 11, the cartridge memory 131, an external connection device, and the like. In addition, the control device 11 can change the head tilt angle according to the dimensional information in the width direction of the magnetic tape during the running. Accordingly, it is possible to bring the effective distance between the servo signal reading elements closer to or match the spacing of the servo bands. The dimensional information can be obtained by using the servo pattern previously formed on the magnetic tape. For example, by doing so, the angle θ formed by the axis of the element array with respect to the width direction of the magnetic tape can be changed during the running of the magnetic tape in the magnetic tape device according to dimensional information of the magnetic tape in the width direction obtained during the running. The head tilt angle can be adjusted, for example, by feedback control. Alternatively, for example, the head tilt angle can also be adjusted by a method disclosed in JP2016-524774A or US2019/0164573A1.

EXAMPLES

Hereinafter, the invention will be described with reference to examples. However, the invention is not limited to the embodiments shown in the examples. “Parts” in the following description indicates “parts by mass”. In addition, steps and evaluations described below are performed in an environment of an atmosphere temperature of 23° C.±1° C., unless otherwise noted. “eq” described below indicates equivalent and a unit not convertible into SI unit.

Projection Formation Agent

A projection formation agent used in the preparation of the magnetic layer forming composition for manufacturing the magnetic tape which will be described later is as follows. A projection formation agent A and a projection formation agent D are particles having a low surface smoothness of a surface of particles. A particle shape of a projection formation agent B is a so-called unspecified shape. A particle shape of a projection formation agent C is a shape of a cocoon. A particle shape of a projection formation agent E is a shape closer to a sphere.

Projection formation agent A: ATLAS (composite particles of silica and polymer) manufactured by Cabot Corporation, average particle size: 100 nm

Projection formation agent B: ASAHI #52 (carbon black) manufactured by Asahi Carbon Co., Ltd., average particle size: 60 nm

Projection formation agent C: TGC6020N (silica particles) manufactured by Cabot Corporation, average particle size: 140 nm

Projection formation agent D: Cataloid (water dispersed sol of silica particles; as a projection formation agent for preparing a magnetic layer forming composition, a dried solid material obtained by removing the solvent by heating the water dispersed sol described above is used) manufactured by JGC c&c, average particle size: 120 nm

Projection formation agent E: PL-10L (water dispersed sol of silica particles; as a projection formation agent for preparing a magnetic layer forming composition, a dried solid material obtained by removing the solvent by heating the water dispersed sol described above is used) manufactured by FUSO CHEMICAL CO., LTD., average particle size: 130 nm

Ferromagnetic Powder

In Table 1, “BaFe” is a hexagonal barium ferrite powder (coercivity Hc: 196 kA/m, an average particle size (average plate diameter): 24 nm).

In Table 1, “SrFe1” is a hexagonal strontium ferrite powder produced by the following method.

1,707 g of SrCO₃, 687 g of H₃BO₃, 1,120 g of Fe₂O₃, 45 g of Al(OH)₃, 24 g of BaCO₃, 13 g of CaCO₃, and 235 g of Nd₂O₃ were weighed and mixed in a mixer to obtain a raw material mixture.

The obtained raw material mixture was dissolved in a platinum crucible at a melting temperature of 1,390° C., and a tap hole provided on the bottom of the platinum crucible was heated while stirring the melt, and the melt was tapped in a rod shape at approximately 6 g/sec. The tap liquid was rolled and cooled with a water cooling twin roller to prepare an amorphous body.

280 g of the prepared amorphous body was put into an electronic furnace, heated to 635° C. (crystallization temperature) at a rate of temperature rise of 3.5° C./min, and held at the same temperature for 5 hours, and hexagonal strontium ferrite particles were precipitated (crystallized).

Then, the crystallized material obtained as described above including the hexagonal strontium ferrite particles was coarse-pulverized with a mortar, 1000 g of zirconia beads having a particle diameter of 1 mm and 800 ml of an acetic acid aqueous solution having a concentration of 1% were added to a glass bottle, and a dispersion process was performed in a paint shaker for 3 hours. After that, the obtained dispersion liquid and the beads were separated and put in a stainless still beaker. The dispersion liquid was left at a liquid temperature of 100° C. for 3 hours, subjected to a dissolving process of a glass component, precipitated with a centrifugal separator, decantation was repeated for cleaning, and drying was performed in a heating furnace at a furnace inner temperature of 110° C. for 6 hours, to obtain hexagonal strontium ferrite powder.

Regarding the hexagonal strontium ferrite powder obtained as described above, an average particle size was 18 nm, an activation volume was 902 nm³, an anisotropy constant Ku was 2.2×10⁵ J/m³, and a mass magnetization σs was 49 A×m²/kg.

12 mg of a sample powder was collected from the hexagonal strontium ferrite powder obtained as described above, the element analysis of a filtrate obtained by the partial dissolving of this sample powder under the dissolving conditions described above was performed by the ICP analysis device, and a surface layer portion content of a neodymium atom was obtained.

Separately, 12 mg of a sample powder was collected from the hexagonal strontium ferrite powder obtained as described above, the element analysis of a filtrate obtained by the total dissolving of this sample powder under the dissolving conditions described above was performed by the ICP analysis device, and a bulk content of a neodymium atom was obtained.

The content (bulk content) of the neodymium atom in the hexagonal strontium ferrite powder obtained as described above with respect to 100 atom % of iron atom was 2.9 atom %. In addition, the surface layer portion content of the neodymium atom was 8.0 atom %. A ratio of the surface layer portion content and the bulk content, “surface layer portion content/bulk content” was 2.8 and it was confirmed that the neodymium atom is unevenly distributed on the surface layer of the particles.

A crystal structure of the hexagonal ferrite shown by the powder obtained as described above was confirmed by scanning CuKα ray under the conditions of a voltage of 45 kV and intensity of 40 mA and measuring an X-ray diffraction pattern under the following conditions (X-ray diffraction analysis). The powder obtained as described above showed a crystal structure of magnetoplumbite type (M type) hexagonal ferrite. In addition, a crystal phase detected by the X-ray diffraction analysis was a magnetoplumbite type single phase.

PANalytical X′Pert Pro diffractometer, PIXcel detector

Soller slit of incident beam and diffraction beam: 0.017 radians

Fixed angle of dispersion slit: ¼ degrees

Mask: 10 mm

Scattering prevention slit: ¼ degrees

Measurement mode: continuous

Measurement time per 1 stage: 3 seconds

Measurement speed: 0.017 degrees per second

Measurement step: 0.05 degree

In Table 1, “SrFe2” is a hexagonal strontium ferrite powder produced by the following method.

1,725 g of SrCO₃, 666 g of H₃BO₃, 1,332 g of Fe₂O₃, 52 g of Al(OH)₃, 34 g of CaCO₃, and 141 g of BaCO₃ were weighed and mixed in a mixer to obtain a raw material mixture.

The obtained raw material mixture was dissolved in a platinum crucible at a melting temperature of 1,380° C., and a tap hole provided on the bottom of the platinum crucible was heated while stirring the melt, and the melt was tapped in a rod shape at approximately 6 g/sec. The tap liquid was rolled and cooled with a water cooling twin roller to prepare an amorphous body.

280 g of the obtained amorphous body was put into an electronic furnace, heated to 645° C. (crystallization temperature), and held at the same temperature for 5 hours, and hexagonal strontium ferrite particles were precipitated (crystallized).

Then, the crystallized material obtained as described above including the hexagonal strontium ferrite particles was coarse-pulverized with a mortar, 1000 g of zirconia beads having a particle diameter of 1 mm and 800 ml of an acetic acid aqueous solution having a concentration of 1% were added to a glass bottle, and a dispersion process was performed in a paint shaker for 3 hours. After that, the obtained dispersion liquid and the beads were separated and put in a stainless still beaker. The dispersion liquid was left at a liquid temperature of 100° C. for 3 hours, subjected to a dissolving process of a glass component, precipitated with a centrifugal separator, decantation was repeated for cleaning, and drying was performed in a heating furnace at a furnace inner temperature of 110° C. for 6 hours, to obtain hexagonal strontium ferrite powder.

Regarding the hexagonal strontium ferrite powder obtained as described above, an average particle size was 19 nm, an activation volume was 1,102 nm³, an anisotropy constant Ku was 2.0×10⁵ J/m³, and a mass magnetization σs was 50 A×m²/kg.

In Table 1, “ε-iron oxide” is an a-iron oxide powder produced by the following method.

4.0 g of ammonia aqueous solution having a concentration of 25% was added to a material obtained by dissolving 8.3 g of iron (III) nitrate nonahydrate, 1.3 g of gallium (III) nitrate octahydrate, 190 mg of cobalt (II) nitrate hexahydrate, 150 mg of titanium (IV) sulfate, and 1.5 g of polyvinyl pyrrolidone (PYP) in 90 g of pure water, while stirring by using a magnetic stirrer, in an atmosphere under the conditions of an atmosphere temperature of 25° C., and the mixture was stirred for 2 hours still under the temperature condition of the atmosphere temperature of 25° C. A citric acid aqueous solution obtained by dissolving 1 g of citric acid in 9 g of pure water was added to the obtained solution and stirred for 1 hour. The powder precipitated after the stirring was collected by centrifugal separation, washed with pure water, and dried in a heating furnace at a furnace inner temperature of 80° C.

800 g of pure water was added to the dried powder and the powder was dispersed in water again, to obtain a dispersion liquid. The obtained dispersion liquid was heated to a liquid temperature of 50° C., and 40 g of ammonia aqueous solution having a concentration of 25% was added dropwise while stirring. The stirring was performed for 1 hour while holding the temperature of 50° C., and 14 mL of tetraethoxysilane (TEOS) was added dropwise and stirred for 24 hours. 50 g of ammonium sulfate was added to the obtained reaction solution, the precipitated powder was collected by centrifugal separation, washed with pure water, and dried in a heating furnace at a furnace inner temperature of 80° C. for 24 hours, and a precursor of ferromagnetic powder was obtained.

The heating furnace at a furnace inner temperature of 1,000° C. was filled with the obtained precursor of ferromagnetic powder in the atmosphere and subjected to heat treatment for 4 hours.

The heat-treated precursor of ferromagnetic powder was put into sodium hydroxide (NaOH) aqueous solution having a concentration of 4 mol/L, the liquid temperature was held at 70° C., stirring was performed for 24 hours, and accordingly, a silicon acid compound which was an impurity was removed from the heat-treated precursor of ferromagnetic powder.

After that, by the centrifugal separation process, ferromagnetic powder obtained by removing the silicon acid compound was collected and washed with pure water, and ferromagnetic powder was obtained.

The composition of the obtained ferromagnetic powder was confirmed by Inductively Coupled Plasma-Optical Emission Spectrometry (ICP-OES), and Ga, Co, and Ti substitution type ε-iron oxide (ε-Ga_(0.28)Co_(0.05)Ti_(0.05)Fe_(1.62)O₃) was obtained. In addition, the X-ray diffraction analysis was performed under the same conditions as disclosed regarding SrFe1 above, and it was confirmed that the obtained ferromagnetic powder has a crystal structure of a single phase which is an a phase not including a crystal structure of an α phase and a γ phase (ε-iron oxide type crystal structure) from the peak of the X-ray diffraction pattern.

Regarding the obtained (ε-iron oxide powder, an average particle size was 12 nm, an activation volume was 746 nm³, an anisotropy constant Ku was 1.2×10⁵ J/m³, and a mass magnetization σs was 16 A×m²/kg.

The activation volume and the anisotropy constant Ku of the hexagonal strontium ferrite powder and the ε-iron oxide powder are values obtained by the method described above regarding each ferromagnetic powder by using an oscillation sample type magnetic-flux meter (manufactured by Toei Industry Co., Ltd.).

The mass magnetization σs is a value measured using an oscillation sample type magnetic-flux meter (manufactured by Toei industry Co., Ltd.) at a magnetic field strength of 15 kOe.

Example A1

Magnetic Layer Forming Composition

Magnetic Liquid

Ferromagnetic powder (see Table 1): 100.0 parts

Oleic acid: 2.0 parts

Vinyl chloride copolymer (MR-104 manufactured by Kaneka Corporation): 10.0 parts

SO₃Na group-containing polyurethane resin: 4.0 parts

(Weight-average molecular weight: 70,000, SO₃Na group: 0.07 meq/g)

Additive A: 10.0 parts

Methyl ethyl ketone: 150.0 parts

Cyclohexanone: 150.0 parts

Abrasive solution

α-alumina (Average particle size: 110 nm): 6.0 parts

Vinyl chloride copolymer (MR 110 manufactured by Kaneka Corporation): 0.7 parts

Cyclohexanone: 20.0 parts

Projection formation agent liquid

Projection formation agent (see Table 1): see Table 1

Methyl ethyl ketone: 9.0 parts

Cyclohexanone: 6.0 parts

Other Components

Polyethyleneimine (manufactured by Nippon Shokubai Co., Ltd., number average molecular weight: 300): 2.0 parts

Stearic acid: 0.5 parts

Stearic acid amide: 0.3 parts

Butyl stearate: 6.0 parts

Methyl ethyl ketone: 110.0 parts

Cyclohexanone: 110.0 parts

Polyisocyanate (CORONATE (registered product) L manufactured by Tosoh Corporation): 3.0 parts

The additive A described above is a polymer synthesized by them method disclosed in paragraphs 0115 to 012.3 of JP2016-051493A.

Non-Magnetic Layer Forming Composition

Non-magnetic inorganic powder (α-iron oxide): 80.0 parts

(Average particle size: 0.15 μm, average acicular ratio: 7, Brunauer-Emmett-Teller (BET) specific surface area: 52 m²/g)

Carbon black (average particle size: 20 nm): 20.0 parts

Electron beam curable vinyl chloride copolymer: 13.0 parts

Electron beam curable polyurethane resin: 6.0 parts

Phenylphosphonic acid: 3.0 parts

Cyclohexanone: 140.0 parts

Methyl ethyl ketone: 170.0 parts

Butyl stearate: 2.0 parts

Stearic acid: 1.0 part

Back Coating Layer Forming Composition

Non-magnetic inorganic powder (α-iron oxide): 80.0 parts

(Average particle size: 0.15 μm, average acicular ratio: 7, BET specific surface area: 52 m²/g)

Carbon black (average particle size: 20 nm): 20.0 parts

Carbon black (average particle size: 100 nm): 3.0 parts

A vinyl chloride copolymer: 13.0 parts

Sulfonic acid group-containing polyurethane resin: 6.0 parts

Phenyiphosphonic acid: 3.0 parts

Cyclohexanone: 140.0 parts

Methyl ethyl ketone: 170.0 parts

Stearic acid: 3.0 parts

Polyisocyanate (CORONATE (registered product) L manufactured by Tosoh Corporation): 5.0 parts

Methyl ethyl ketone: 400.0 parts

Preparation of Each Layer Forming Composition

The magnetic layer forming composition was prepared by the following method.

The components of the magnetic liquid were kneaded by an open kneader and diluted, and was subjected to a dispersion process of 12 passes, with a transverse beads mill disperser and zirconia (ZrO₂) beads having a particle diameter of 0.5 mm (hereinafter, referred to as “Zr beads”), by setting a bead filling percentage as 80 volume %, a circumferential speed of rotor distal end as 10 m/sec, and a retention time for 1 pass for 2 minutes.

Regarding the abrasive solution, components of the abrasive solution were mixed and put in a vertical sand mill disperser together with Zr beads having a particle diameter of 1 mm, so as to perform the adjustment so that a value of bead volume/(abrasive solution volume+bead volume) was 60%, the sand mill dispersion process was performed for 180 minutes, the liquid after the process was extracted, and an ultrasonic dispersion filtering process was performed by using a flow type ultrasonic dispersion filtering device. The projection formation agent liquid was prepared by filtering a dispersion liquid obtained by mixing the components of the above-mentioned projection formation agent liquid and then ultrasonically treating (dispersing) for 60 minutes with an ultrasonic output of 500 watts per 200 cc by a horn-type ultrasonic dispersing device with a filter having a hole size of 0.5 μm.

The magnetic liquid, the abrasive solution, the projection formation agent liquid, and the other components were introduced in a dissolver stirrer, and stirred at a circumferential speed of 10 m/sec for 30 minutes. Then, a process at a flow rate of 7.5 kg/min was performed for 3 passes with a flow type ultrasonic disperser, and then, the mixture was filtered with a filter having a hole diameter of 1 μm, to prepare a magnetic layer forming composition.

The non-magnetic layer forming composition was prepared by the following method.

The components excluding the lubricant (butyl stearate and stearic acid) were kneaded and diluted with an open kneader, and then dispersed with a transverse beads mill disperser. Then, the lubricant (butyl stearate and stearic acid) was added, and the mixture was stirred and mixed with a dissolver stirrer to prepare a non-magnetic layer forming composition.

The back coating layer forming composition was prepared by the following method.

The components excluding the lubricant (stearic acid), polyisocyanate, and methyl ethyl ketone (400.0 parts) were kneaded and diluted with an open kneader, and then dispersed with a transverse beads mill disperser. Then, the lubricant (stearic acid), polyisocyanate, and methyl ethyl ketone (400.0 parts) were added, and the mixture was stirred and mixed with a dissolver stirrer to prepare a back coating layer forming composition.

Manufacturing of Magnetic Tape and Magnetic Tape Cartridge

The non-magnetic layer forming composition was applied to a biaxial stretching support made of polyethylene naphthalate having a thickness shown in Table 1 so that the thickness after the drying is a thickness shown in Table 1 and was dried to emit an electron ray to have energy of 40 kGy at an acceleration voltage of 125 kV. The magnetic layer forming composition was applied onto that so that the thickness after the drying is a thickness shown in Table 1 and dried, and the back coating layer forming composition was applied to a surface of the support opposite to the surface where the non-magnetic layer and the magnetic layer are formed, so that the thickness after the drying is a thickness shown in Table 1 and dried.

Then, a calender process was performed by using a 7-stage calender roll configured of only a metal roll, at a calendar speed of 80 m/min, linear pressure of 294 kN/m, and a calender temperature (surface temperature of a calender roll) of 80° C. Then, the heat treatment was performed in the environment of the ambient temperature of 70° C. for 36 hours. After heat treatment, the slitting was performed so as to have a width of ½ inches, and the surface of the magnetic layer was cleaned with a tape cleaning device in which a nonwoven fabric and a razor blade are attached to a device including a sending and winding devices of the slit product to press the surface of the magnetic layer, and the magnetic tape was obtained.

By recording a servo signal on a magnetic layer of the obtained magnetic tape with a commercially available servo writer, and including a servo pattern (timing-based servo pattern) having the disposition and shape according to the linear tape-open (LTO) Ultrium format on the servo band was obtained.

Accordingly, a magnetic tape including data bands, servo bands, and guide bands in the disposition according to the LTO Ultrium format in the magnetic layer, and including servo patterns (timing-based servo pattern) having the disposition and the shape according to the LTO Ultrium format on the servo band was obtained. The servo pattern formed by doing so is a servo pattern disclosed in Japanese industrial Standards (JIS) X6175:2006 and Standard ECMA-319 (June 2001).

The total number of servo bands is five, and the total number of data bands is four.

A magnetic tape (length of 960 m) on which the servo signal was recorded as described above was wound around the reel of the magnetic tape cartridge (LIC) Ultrium 8 data cartridge), and a leader tape according to Article 9 of Section 3 of standard European Computer Manufacturers Association (ECMA)-319 (June 2001) was bonded to an end thereof by using a commercially available splicing tape.

By doing so, a magnetic tape cartridge in which the magnetic tape was wound around the reel was manufactured.

It can be confirmed by the following method that the magnetic layer of the magnetic tape contains a compound formed of polyethyleneimine and stearic acid and having an ammonium salt structure of an alkyl ester anion represented by Formula 1.

A sample is cut out from a magnetic tape, and X-ray photoelectron spectroscopy analysis is performed on the surface of the magnetic layer (measurement area: 300 μm×700 μm) using an ESCA device. Specifically, wide scan measurement is performed by the ESCA device under the following measurement conditions. In the measurement results, peaks are confirmed at a position of a binding energy of the ester anion and a position of a binding energy of the ammonium cation.

Device: AXIS-ULTRA manufactured by Shimadzu Corporation

Excited X-ray source: Monochromatic Al-Kα ray

Scan range: 0 to 1,200 eV

Pass energy: 160 eV

Energy resolution: 1 eV/step

Capturing Time: 100 ms/step

Number of times of integration: 5

In addition, a sample piece having a length of 3 cm is cut out from the magnetic tape, and attenuated total reflection-Fourier transform-infrared spectrum (ATR-FT-IR) measurement. (reflection method) is performed on the surface of the magnetic layer, and, in the measurement result, the absorption is confirmed on a wave number corresponding to absorption of COO⁻ (1,540 cm⁻¹ or 1,430 cm⁻¹) and a wave number corresponding to the absorption of the ammonium cation (2,400 cm⁻¹).

Example A2 to Example A27 and Example B1 to Example B34

A magnetic tape and a magnetic tape cartridge were obtained by the method described in Example A1, except that the items shown in Table 1 were changed as shown in Table 1.

For Examples A23 to A27 and Comparative Examples B30 to B34, the step after recording the servo signal was changed as follows. That is, the heat treatment was performed after recording the servo signal. On the other hand, in Examples A1 to A22 and Comparative Examples B1 to B29, since such heat treatment was not performed, “None” was shown in the column of “heat treatment condition” in Table 1.

For Examples A23 to A27 and Comparative Examples B30 to B34, the magnetic tape (length of 970 m) after recording the servo signal as described in Example A1 was wound around a core for heat treatment and heat-treated in a state of being wound around the core. As the core for heat treatment, a solid core member (outer diameter: 50 mm) formed of a resin and having a value of a modulus of bending elasticity shown in Table 1 was used, and the tension in a case of the winding was set as a value shown in Table 1. The heat treatment temperature and heat treatment time in the heat treatment were set to values shown in Table 1. The weight absolute humidity in the atmosphere in which the heat treatment was performed was 10 g/kg Dry air.

After the heat treatment, the magnetic tape and the core for heat treatment were sufficiently cooled, the magnetic tape was detached from the core for heat treatment and wound around the core for temporary winding, and then, the magnetic tape having the final product length (960 m) was wound around the reel of the magnetic tape cartridge (LTO Ultrium 8 data cartridge) from the core for temporary winding. The remaining length of 10 m was cut out and the leader tape based on section 9 of Standard European Computer Manufacturers Association (ECMA)-319 (June 2001) Section 3 was bonded to the end of the cut side by using a commercially available splicing tape.

As the core for temporary winding, a solid core member having the same outer diameter and formed of the same material as the core for heat treatment was used, and the tension at the time of winding was set as 0.6 N.

By doing so, a magnetic tape cartridge in which the magnetic tape was wound around the reel was manufactured.

For each example, four magnetic tape cartridges were manufactured, one was used for the evaluation of running stability below, and the other three were used for the evaluations (1) to (3) of the magnetic tape.

Evaluation of Magnetic Tape

(1) Frictional Force

The magnetic tape was extracted from each of the magnetic tape cartridges of each example, and the frictional force F_(45°) and the standard deviation of the frictional three F were obtained by the method described above in the environment with the temperature of 32° C. and the relative humidity of 80%. As the LTO8 head, a commercially available LTO8 head (manufactured by IBM) was used.

(2) Standard Deviation of Curvature of Magnetic Tape in Longitudinal Direction

The magnetic tape was taken out from the magnetic tape cartridge of each example, and the standard deviation of the curvature of the magnetic tape in the longitudinal direction was determined by the method described above.

(3) Tape Thickness

10 tape samples (length: 5 cm) were cut out from any part of the magnetic tape taken out from the magnetic tape cartridge of each example, and these tape samples were stacked to measure the thickness. The thickness was measured using a digital thickness gauge of a Millimar 1240 compact amplifier manufactured by MARE and a Millimar 1301 induction probe. The value (thickness per tape sample) obtained by calculating 1/10 of the measured thickness was defined as the tape thickness.

Evaluation of Running Stability

In an environment, with a temperature of 32° C. and a relative humidity of 80%, the. running stability was evaluated by the following method.

Using each of the magnetic tape cartridges of each example, data recording and reproducing were performed using the magnetic tape device having the configuration shown in FIG. 8 . The arrangement order of the modules included in the recording and reproducing head mounted on the recording and reproducing head unit is “recording module-reproducing module-recording module” (total number of modules: 3). The number of magnetic head elements in each module is 32 (Ch0 to Ch31), and the element array is configured by sandwiching these magnetic head elements between the pair of servo signal reading elements. The reproducing element width of the reproducing element included in the reproducing module is 0.8 μm.

By the following method, the performing of the recording and reproducing of data and evaluating of the running stability during the reproducing were performed four times in total by sequentially changing the head tilt angle in the order of 0°, 15°, 30°, and 45°. The head tilt angle is an angle θ formed by the axis of the element array of the reproducing module with respect to the width direction of the magnetic tape at the start of each time of running. The angle θ was set by the control device of the magnetic tape device at the start of each time of running of the magnetic tape, and the head tilt angle was fixed during each time of running of the magnetic tape.

The magnetic tape cartridge was set in the magnetic tape device and the magnetic tape was loaded. Next, while performing servo tracking, the recording and reproducing head unit records pseudo random data having a specific data pattern on the magnetic tape. The tension applied in the tape longitudinal direction at that time is a constant value. At the same time with the recording of the data, the value of the servo band spacing of the entire tape length was measured every 1 m of the longitudinal position and recorded in the cartridge memory.

Next, while performing servo tracking, the recording and reproducing head unit reproduces the data recorded on the magnetic tape. The tension applied in the tape longitudinal direction at that time is a constant value.

The running stability was evaluated using a standard deviation of a reading position PES (Position Error Signal) in the width direction based on the servo signal obtained by the servo signal reading element during the reproducing (hereinafter, referred to as “σPES”) as an indicator.

PES is obtained by the following method.

In order to obtain the PES, the dimensions of the servo pattern are required. The standard of the dimension of the servo pattern varies depending on generation of LTO. Therefore, first, an average distance AC between the corresponding four stripes of the A burst and the C burst and an azimuth angle α of the servo pattern are measured using a magnetic force microscope or the like.

An average time between 5 stripes corresponding to the A burst and the B burst over the length of 1 LPOS word is defined as a. An average time between 4 stripes corresponding to the A burst and the C burst over the length of 1 LPOS word is defined as b. At this time, the value defined by AC×(½−a/b)/(2×tan(α)) represents a reading position PES (Position Error Signal) in the width direction based on the servo signal obtained by the servo signal reading element over the length of 1 LPOS word. Regarding the magnetic tape, an end on a side wound around a reel of the magnetic tape cartridge is referred to as an inner end, an end on the opposite side thereof is referred to as an outer end, the outer end is set to 0 m, and in a region in a tape longitudinal direction over a length of 30 m to 200 m, the standard deviation of PES (σPES) obtained by the method described above was calculated.

The arithmetic average of σPES obtained during four times of recording and reproducing in total is shown in the column of “σPES” in Table 1. In a case where the σPES is less than 70 nm, it can be determined that the running stability is excellent.

Recording Capacity

In each example, even in a case where the tape thickness of the magnetic tape is different, the magnetic tape having the same length was accommodated in the magnetic tape cartridge.

On the other hand, since the magnetic tape cartridge generally accommodates the magnetic tape in a state of being wound around a reel in a housing, it cannot accommodate the magnetic tape having a volume exceeding the volume in the housing. As the tape thickness of the magnetic tape is large, the tape volume per unit length further increases, and accordingly, a maximum tape length that can be accommodated in the housing is short.

Regarding the recording capacity, as the magnetic tape having a longer tape length is accommodated in one reel of the magnetic tape cartridge, the recording capacity per one reel of the magnetic tape cartridge can be further increased.

From the above description, a magnetic tape having a longer maximum tape length that can be accommodated in the housing having a certain volume is more preferable for high capacity, and such a maximum tape length decreases, as the tape thickness of the magnetic tape is large. Accordingly, the recording capacity of the magnetic tapes of each of the above examples was evaluated as follows.

The magnetic tape of Example B12 having a tape thickness of 5.6 μm is used as a standard for recording capacity (following evaluation indicator: 100).

For a magnetic tape having a tape thickness of T μm, the evaluation indicator (no unit) of the recording capacity is calculated as “evaluation indicator=(5.6−T)/5.6×100+100”. It can be said that a magnetic tape in which the value calculated as described above is large is more preferable for high capacity.

The result described above is shown in Table 1 (Tables 1-1 and 1-2).

TABLE 1-1 Magnetic layer forming composition Polyethyleneimine Stearic acid Magnetic Non-magnetic Ferromagnetic Present Present Tape layer layer powder or absent or absent Projection formation agent thickness thickness thickness Kind of adding of adding Kind Amount μm μm μm Example A1 BaFe Added Added Projection 1.0 part by mass 5.2 0.1 0.5 formation agent A Example A2 BaFe Added Added Projection 1.0 part by mass 5.0 0.1 0.5 formation agent A Example A3 BaFe Added Added Projection 1.0 part by mass 4.5 0.1 0.5 formation agent A Example A4 BaFe Added Added Projection 1.0 part by mass 4.2 0.1 0.2 formation agent A Example A5 BaFe Added Added Projection 1.0 part by mass 4.0 0.1 0.2 formation agent A Example A6 BaFe Added Added Projection 1.0 part by mass 5.2 0.1 0.5 formation agent B Example A7 BaFe Added Added Projection 1.0 part by mass 5.2 0.1 0.5 formation agent C Example A8 BaFe Added Added Projection 1.0 part by mass 5.2 0.1 0.5 formation agent D Example A9 BaFe Added Added Projection 2.0 parts by mass 5.2 0.1 0.5 formation agent A Example A10 BaFe Added Added Projection 3.0 parts by mass 5.2 0.1 0.5 formation agent A Example A11 BaFe Added Added Projection 4.0 parts by mass 5.2 0.1 0.5 formation agent A Example A12 BaFe Added Added Projection 2.0 parts by mass 5.2 0.1 0.5 formation agent B Example A13 BaFe Added Added Projection 3.0 parts by mass 4.5 0.1 0.5 formation agent B Example A14 BaFe Added Added Projection 2.0 parts by mass 5.2 0.1 0.5 formation agent C Example A15 BaFe Added Added Projection 3.0 parts by mass 5.2 0.1 0.5 formation agent C Example A16 BaFe Added Added Projection 4.0 parts by mass 5.2 0.1 0.5 formation agent C Example A17 BaFe Added Added Projection 2.0 parts by mass 5.2 0.1 0.5 formation agent D Example A18 BaFe Added Added Projection 3.0 parts by mass 5.2 0.1 0.5 formation agent D Example A19 BaFe Added Added Projection 4.0 parts by mass 5.2 0.1 0.5 formation agent D Example A20 SrFe1 Added Added Projection 1.0 part by mass 5.2 0.1 0.5 formation agent A Example A21 SrFe2 Added Added Projection 1.0 part by mass 5.2 0.1 0.5 formation agent A Example A22 ε- Added Added Projection 1.0 part by mass 5.2 0.1 0.5 iron formation oxide agent A Example A23 BaFe Added Added Projection 1.0 part by mass 4.0 0.1 0.2 formation agent A Example A24 BaFe Added Added Projection 1.0 part by mass 4.0 0.1 0.2 formation agent A Example A25 BaFe Added Added Projection 1.0 part by mass 4.0 0.1 0.2 formation agent A Example A26 BaFe Added Added Projection 1.0 part by mass 4.0 0.1 0.2 formation agent A Example A27 BaFe Added Added Projection 4.0 parts by mass 4.0 0.1 0.2 formation agent A Heat treatment conditions Back Non- Modulus Tension Standard coating magnetic of in case of Standard deviation layer support bending winding deviation of thickness thickness elasticity around F_(45°) of F curvature σPES Recording μm μm Temperature Time for core the core (gf) (gf) (mm/m) (nm) capacity Example A1 0.5 4.1 None None None None 15 10 6 55 107 Example A2 0.3 4.1 None None None None 15 10 6 55 111 Example A3 0.3 3.6 None None None None 15 10 6 55 120 Example A4 0.3 3.6 None None None None 15 10 6 57 125 Example A5 0.2 3.5 None None None None 15 10 6 58 129 Example A6 0.5 4.1 None None None None 14 10 6 53 107 Example A7 0.5 4.1 None None None None 13 9 6 51 107 Example A8 0.5 4.1 None None None None 13 9 6 54 107 Example A9 0.5 4.1 None None None None 10 7 6 50 107 Example A10 0.5 4.1 None None None None 7 5 6 40 107 Example A11 0.5 4.1 None None None None 4 2 6 35 107 Example A12 0.5 4.1 None None None None 13 8 6 49 107 Example A13 0.3 3.6 None None None None 9 5 6 45 120 Example A14 0.5 4.1 None None None None 10 7 6 47 107 Example A15 0.5 4.1 None None None None 8 5 6 43 107 Example A16 0.5 4.1 None None None None 4 2 6 38 107 Example A17 0.5 4.1 None None None None 11 7 6 50 107 Example A18 0.5 4.1 None None None None 7 4 6 45 107 Example A19 0.5 4.1 None None None None 4 2 6 33 107 Example A20 0.5 4.1 None None None None 15 10 6 55 107 Example A21 0.5 4.1 None None None None 15 10 6 55 107 Example A22 0.5 4.1 None None None None 15 10 6 55 107 Example A23 0.2 3.5 50° C. 5 hours 0.8 GPa 0.6N 15 10 5 50 129 Example A24 0.2 3.5 60° C. 5 hours 0.8 GPa 0.6N 15 10 4 47 129 Example A25 0.2 3.5 70° C. 5 hours 0.8 GPa 0.6N 15 10 3 45 129 Example A26 0.2 3.5 70° C. 15 hours  0.8 GPa 0.8N 15 10 2 43 129 Example A27 0.2 3.5 70° C. 15 hours  0.8 GPa 0.8N 4 2 2 30 129

TABLE 1-2 Magnetic layer forming composition Stearic Non- Back Polyethyleneimine acid Magnetic magnetic coating Ferromagnetic Present Present Tape layer layer layer powder or absent or absent Projection formation agent thickness thickness thickness thickness Kind of adding of adding Kind Amount μm μm μm μm Example B1 BaFe None Added Projection 1.0 part by mass 6.1 0.1 0.9 0.5 formation agent E Example B2 BaFe None Added Projection 1.5 parts by mass 6.1 0.1 0.9 0.5 formation agent E Example B3 BaFe Added Added Projection 1.0 part by mass 6.1 0.1 0.9 0.5 formation agent E Example B4 BaFe None Added Projection 1.0 part by mass 6.1 0.1 0.9 0.5 formation agent A Example B5 BaFe None Added Projection 2.0 parts by mass 6.1 0.1 0.9 0.5 formation agent A Example B6 BaFe None Added Projection 3.0 parts by mass 6.1 0.1 0.9 0.5 formation agent A Example B7 BaFe None Added Projection 2.0 parts by mass 6.1 0.1 0.9 0.5 formation agent B Example B8 BaFe None Added Projection 3.0 parts by mass 6.1 0.1 0.9 0.5 formation agent B Example B9 BaFe None Added Projection 3.0 parts by mass 6.1 0.1 0.9 0.5 formation agent C Example B10 BaFe None Added Projection 0.5 parts by mass 6.1 0.1 0.9 0.5 formation agent E Example B11 BaFe Added Added Projection 5.0 parts by mass 6.1 0.1 0.9 0.5 formation agent A Example B12 BaFe Added Added Projection 1.0 part by mass 5.6 0.1 0.9 0.4 formation agent A Example B13 BaFe Added Added Projection 1.0 part by mass 5.6 0.1 0.8 0.4 formation agent B Example B14 BaFe Added Added Projection 1.0 part by mass 5.6 0.1 0.8 0.4 formation agent C Example B15 BaFe Added Added Projection 1.0 part by mass 5.6 0.1 0.8 0.4 formation agent D Example B16 BaFe Added Added Projection 2.0 parts by mass 5.6 0.1 0.8 0.4 formation agent A Example B17 BaFe Added Added Projection 3.0 parts by mass 5.6 0.1 0.8 0.4 formation agent A Example B18 BaFe Added Added Projection 4.0 parts by mass 5.6 0.1 0.8 0.4 formation agent A Example B19 BaFe Added Added Projection 2.0 parts by mass 5.6 0.1 0.8 0.4 formation agent B Example B20 BaFe Added Added Projection 3.0 parts by mass 5.6 0.1 0.8 0.4 formation agent B Example B21 BaFe Added Added Projection 2.0 parts by mass 5.6 0.1 0.8 0.4 formation agent C Example B22 BaFe Added Added Projection 3.0 parts by mass 5.6 0.1 0.8 0.4 formation agent C Example B23 BaFe Added Added Projection 4.0 parts by mass 5.6 0.1 0.8 0.4 formation agent C Example B24 BaFe Added Added Projection 2.0 parts by mass 5.6 0.1 0.8 0.4 formation agent D Example B25 BaFe Added Added Projection 3.0 parts by mass 5.6 0.1 0.8 0.4 formation agent D Example B26 BaFe Added Added Projection 4.0 parts by mass 5.6 0.1 0.8 0.4 formation agent D Example B27 SrFe1 Added Added Projection 1.0 part by mass 5.6 0.1 0.8 0.4 formation agent A Example B28 SrFe2 Added Added Projection 1.0 part by mass 5.6 0.1 0.8 0.4 formation agent A Example B29 ε-iron Added Added Projection 1.0 part by mass 5.6 0.1 0.8 0.4 oxide formation agent A Example B30 BaFe Added Added Projection 1.0 part by mass 5.6 0.1 0.8 0.4 formation agent A Example B31 BaFe Added Added Projection 1.0 part by mass 5.6 0.1 0.8 0.4 formation agent A Example B32 BaFe Added Added Projection 1.0 part by mass 5.6 0.1 0.8 0.4 formation agent A Example B33 BaFe Added Added Projection 1.0 part by mass 5.6 0.1 0.8 0.4 formation agent A Example B34 BaFe Added Added Projection 4.0 parts by mass 5.6 0.1 0.8 0.4 formation agent A Heat treatment conditions Non- Tension magnetic Modulus of in case Standard Standard support bending of winding deviation deviation of thickness elasticity around F_(45°) of F curvature σPES Recording μm Temperature Time for core the core (gf) (gf) (mm/m) (nm) capacity Example B1 4.6 None None None None 20 15 6 78 91 Example B2 4.6 None None None None 19 17 6 73 91 Example B3 4.6 None None None None 19 13 6 76 91 Example B4 4.6 None None None None 20 17 6 77 91 Example B5 4.6 None None None None 17 16 6 78 91 Example B6 4.6 None None None None 19 16 6 75 91 Example B7 4.6 None None None None 16 11 6 76 91 Example B8 4.6 None None None None 16 11 6 75 91 Example B9 4.6 None None None None 16 11 6 75 91 Example B10 4.6 None None None None 19 15 6 85 91 Example B11 4.6 None None None None 3 2 6 73 91 Example B12 4.3 None None None None 15 10 6 55 100 Example B13 4.3 None None None None 14 10 6 53 100 Example B14 4.3 None None None None 13 9 6 51 100 Example B15 4.3 None None None None 13 9 6 54 100 Example B16 4.3 None None None None 10 7 6 50 100 Example B17 4.3 None None None None 7 5 6 40 100 Example B18 4.3 None None None Norte 4 2 6 35 100 Example B19 4.3 None None None None 13 8 6 49 100 Example B20 4.3 None None None None 9 5 6 45 100 Example B21 4.3 None None None None 10 7 6 47 100 Example B22 4.3 None None None None 8 5 6 43 100 Example B23 4.3 None None None None 4 2 6 38 100 Example B24 4.3 None None None None 11 7 6 50 100 Example B25 4.3 None None None None 7 4 6 45 100 Example B26 4.3 None None None None 4 2 6 33 100 Example B27 4.3 None None None None 15 10 6 55 100 Example B28 4.3 None None None None 15 10 6 55 100 Example B29 4.3 None None None None 15 10 6 55 100 Example B30 4.3 50° C. 5 hours 0.8 GPa 0.6N 15 10 5 50 100 Example B31 4.3 60° C. 5 hours 0.8 GPa 0.6N 15 10 4 47 100 Example B32 4.3 70° C. 5 hours 0.8 GPa 0.6N 15 10 3 45 100 Example B33 4.3 70° C. 15 hours  0.8 GPa 0.8N 15 10 2 43 100 Example B34 4.3 70° C. 15 hours  0.8 GPa 0.8N 4 2 2 30 100

From the results shown in Table 1, it can be confirmed that the magnetic tapes of Examples A1 to Examples A27 showed excellent running stability in a case where the magnetic tape was allowed to run at different head tilt angles in the high temperature and high humidity environment and it is preferable from a viewpoint of increasing the recording capacity.

The magnetic tape cartridge P-1 was manufactured by the method described in Example A1, except that, during the manufacturing of the magnetic tape, after forming the coating layer by applying the magnetic layer forming composition, a homeotropic alignment process was performed by applying a magnetic field having a magnetic field strength of 0.3 T in a vertical direction with respect to a surface of a coating layer, while the coating layer of the magnetic layer forming composition is wet, and then, the drying was performed to form the magnetic layer.

The magnetic tape cartridge P-2 was manufactured by the method described in Example A2, except that, during the manufacturing of the magnetic tape, after forming the coating layer by applying the magnetic layer forming composition, a homeotropic alignment process was performed by applying a magnetic field having a magnetic field strength of 0.5 T in a vertical direction with respect to a surface of a coating layer, while the coating layer of the magnetic layer forming composition is wet, and then, the drying was performed to form the magnetic layer.

A sample piece was cut out from the magnetic tape taken out from the magnetic tape cartridge P-1. For this sample piece, a vertical squareness ratio was measured by the method described above using a TM-TRVSM5050-SMSL type manufactured by Tamagawa Seisakusho Co., Ltd. as an oscillation sample type magnetic-flux meter. The vertical squareness ratio thus measured was 0.60.

A sample piece was cut out from the magnetic tape taken out from the magnetic tape cartridge P-2. For this sample piece, the vertical squareness ratio was measured in the same manner as described above. The vertical squareness ratio thus measured was 0.65.

The magnetic tape was also taken out from the magnetic tape cartridge of Example A1. For this sample piece, the vertical squareness ratio was measured in the same manner as described above. The vertical squareness ratio thus measured was 0.55.

Each of the magnetic tapes taken out from the above three magnetic tape cartridges was attached to each of the ½-inch reel testers, and the electromagnetic conversion characteristics (signal-to-noise ratio (SNR)) were evaluated by the following methods. As a result, regarding the magnetic tape taken out from the magnetic tape cartridge P-1 (manufactured by performing the homeotropic alignment process), a value of SNR 2 dB higher than that of the magnetic tape taken out from the magnetic tape cartridge of Example A1 without the homeotropic alignment process was obtained. Regarding the magnetic tape taken out from the magnetic tape cartridge P-2 (manufactured by performing the homeotropic alignment process), a value of SNR 4 dB higher than that of the magnetic tape taken out from the magnetic tape cartridge of Example A1.

In an environment of a temperature of 23° C. and a relative humidity of 50%, a tension of 0.7 N was applied in the longitudinal direction of the magnetic tape, and recording and reproduction were performed for 10 passes. A relative speed of the magnetic head and the magnetic tape was set as 6 m/sec. The recording was performed by using a metal-in-gap (MIG) head (gap length of 0.15 μm, track width of 1.0 μm) as the recording head and by setting a recording current as an optimal recording current of each magnetic tape. The reproduction was performed using a giant-magnetoresistive (GMR) head (element thickness of 15 nm, shield interval of 0.1 μm, reproducing element width of 0.8 μm) as the reproduction head. The head tilt angle was set to 0°. A signal having a linear recording density of 300 kfci was recorded, and the reproduction signal was measured with a spectrum analyzer manufactured by ShibaSoku Co., Ltd. In addition, the unit kfci is a unit of linear recording density (cannot be converted to SI unit system). As the signal, a sufficiently stabilized portion of the signal after starting the running of the magnetic tape was used.

One aspect of the invention is advantageous in a technical field of various data storages. 

What is claimed is:
 1. A magnetic tape comprising: a non-magnetic support; and a magnetic layer containing a ferromagnetic powder, wherein a tape thickness of the magnetic tape is 5.2 μm or less, in an environment with a temperature of 32° C. and a relative humidity of 80%, a frictional force F_(45°) on a surface of the magnetic layer with respect to an LTO8 head measured at a head tilt angle of 45° is 4 gf to 15 gf, and a standard deviation of a frictional force F on the surface of the magnetic layer with respect to the LTO8 head measured at each of head tilt angles of 0°, 15°, 30°, and 45° is 10 gf or less.
 2. The magnetic tape according to claim 1, wherein the standard deviation of F is 2 gf to 10 gf.
 3. The magnetic tape according to claim 1, wherein the tape thickness is 4.0 μm to 5.2 μm.
 4. The magnetic tape according to claim 1, wherein the tape thickness is 4.0 μm to 5.0 μm.
 5. The magnetic tape according to claim 1, wherein a standard deviation of curvature of the magnetic tape in a longitudinal direction is 5 mm/m or less.
 6. The magnetic tape according to claim 1, wherein the magnetic layer contains inorganic oxide-based particles.
 7. The magnetic tape according to claim 6, wherein the inorganic oxide-based particles are composite particles of an inorganic oxide and a polymer.
 8. The magnetic tape according to claim 1, wherein the magnetic layer contains carbon black.
 9. The magnetic tape according to claim 1, further comprising: a non-magnetic layer containing a non-magnetic powder between the non-magnetic support and the magnetic layer.
 10. The magnetic tape according to claim 9, wherein a thickness of the non-magnetic layer is 0.1 μm to 0.7 μm.
 11. The magnetic tape according to claim 1, further comprising: a back coating layer containing a non-magnetic powder on a surface side of the non-magnetic support opposite to a surface side provided with the magnetic layer.
 12. The magnetic tape according to claim 1, wherein a vertical squareness ratio of the magnetic tape is 0.60 or more.
 13. The magnetic tape according to claim 1, wherein a vertical squareness ratio of the magnetic tape is 0.60 or more.
 14. A magnetic tape cartridge comprising: the magnetic tape according to claim
 1. 15. A magnetic tape device comprising: the magnetic tape according to claim
 1. 16. The magnetic tape device according to claim 15, further comprising: a magnetic head, wherein the magnetic head includes a module having an element array including a plurality of magnetic head elements between a pair of servo signal reading elements, and the magnetic tape device changes an angle θ formed by an axis of the element array with respect to a width direction of the magnetic tape during running of the magnetic tape in the magnetic tape device. 